Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 206 MPa | 29900 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RX05491 PA 66 LNP* Thermocomp* RX05491 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 206 MPa | 29900 psi | ISO 527 |
SABIC Innovative Plastics LNP VERTON RV008ES PA 66 LNP* VERTON* RV008ES is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural. |
|||
Tensile Strength at Break | 206 MPa | 29900 psi | ISO 527 |
SABIC Innovative Plastics LNP VERTON RV008ES PA 66 (Asia Pacific) LNP* Verton* RV008ES is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
Tensile Strength at Break | 206 MPa | 29900 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON RVL28 PA 66 (Asia Pacific) LNP VERTON* RVL28 is a compound based on Nylon 66 resin containing Long Glass Fiber, PTFE. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 206 MPa | 29900 psi | ISO 527-2 |
Ascend Performance Materials VYDYNE® R533H Nylon, 33% Glass Reinforced, DAM Vydyne® R533H is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-free.. |
|||
Tensile Strength at Break | 206 MPa | 29900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON RX00327 PA 66 LNP* VERTON* RX00327 is a compound based on Nylon 66 resin containing proprietary fillers. Added feature of this material is: Structural. |