- Polymer Property : Tensile Strength at Break = 2800 psi
Polymer Property : Tensile Strength at Break = 2800 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.3 MPa | 2800 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable W1604L-xx07FRD Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable WJAC38 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Wire & Cable WJJC330 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
| RheTech Products FT1002-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
| RheTech Products FT1003-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Step and hitch padsInterior component and trimA/B pillarsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
| RheTech Products FT4702-527UV Thermoplastic Polyolefin, UV Stabilized, XS9 Dark Neutral Metallic Applications: Exterior door moldingsRigid bumper coversBodyside claddings and fairingsAutomotive grillesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
| RheTech Products FT4702-715UV Thermoplastic Polyolefin, UV Stabilized, ZSP Deep Grey Applications: Exterior componentsGrillesBumper trimDoor componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R1700E Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D4894 |
| 3M Dyneon™ CC503 PTFE, 15% Mineral Filled
(discontinued **) Product Form: White, pelletized free-flowing powder. Applications include bearings - FDA compliant, valve seats, seals.Data provided by Dyneon. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D4894 |
| 3M Dyneon™ CC622 PTFE 10% Graphite Filled
(discontinued **) Product Form: Black, pelletized free-flowing powder. Applications include bearings, ring seals.Data provided by Dyneon. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D1414 |
| Greene Tweed FLUORAZ® 797 Fluoroelastomer, FEPM Greene, Tweed`s Fluoraz® functions effortlessly in a variety of challenging process environments. Fluoraz performs well in aggressive chemicals where ultrapure materials are not required. Known f.. |
|||
| Tensile Strength at Break | >= 19.3 MPa | >= 2800 psi | ASTM D412 Method A |
| Seals Eastern 7182X Fluorocarbon-Elastomer Formulated AFLAS®. Ultra-low compressive stress relaxation for alkaline, high-temperature service.Information provided by Seals Eastern, Inc. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
| Teknor Apex APEX® 84458 Polyvinyl Chloride, Flexible Notes: 105°C Insulation; RoHS Compliant Features: Flame Retardant Uses: InsulationAgency Ratings: UL 1063; UL 1581; UL 62 Forms: Pellets Wire Types: AWMInformation Provided by Teknor Apex |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
| Teknor Apex APEX® 65006 Polyvinyl Chloride, Flexible Notes: 75°C Jacket; RoHS Compliant Uses: Wire and Cable ApplicationsForms: PelletsInformation Provided by Teknor Apex |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
| Teknor Apex APEX® 84856 Polyvinyl Chloride, Flexible Notes: 90°C Insulation; RoHS Compliant Features: Flame Retardant; Sunlight Resistant (720 hours) Uses: Cable JacketingAgency Ratings: UL 62; UL QMTT2 .E73402 Forms: Pellets Wire Types: SJTW; STWI.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
| Plastics Group Polifil® BS-70 70% Barium Sulfate Reinforced Polypropylene Polifil® BS series compounds are homopolymer polypropylene resins reinforced with barium sulfate. They possess increased specific gravity, high flex modulus, high deflection temperature, good chemi.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
| A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 15 s set time |
| Elmer's Products Aron Alpha® 201 Cyanoacrylate Adhesive (Industrial Krazy Glue™) General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 60 s set time |
| Elmer's Products Aron Alpha® 202 Cyanoacrylate Adhesive (Industrial Krazy Glue™) General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Medium gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 60 s set time |
| Elmer's Products Aron Alpha® 212E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.Medium gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous s.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 10 s set time |
| Elmer's Products Aron Alpha® 221 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 15 s set time |
| Elmer's Products Aron Alpha® 232 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 15 s set time |
| Elmer's Products Aron Alpha® 241F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 15 s set time |
| Elmer's Products Aron Alpha® 282F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 60 s set time |
| Elmer's Products Aron Alpha® 241 Cyanoacrylate Adhesive (Industrial Krazy Glue™) General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 60 s set time |
| Elmer's Products Aron Alpha® 252E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous sub.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
| Americas Styrenics STYRON A-TECH® 1115 High Impact Polystyrene Product CharacteristicsHigh Gloss/High ImpactConsistent colorabilityEasy processingFood Contact CompliantTypical ApplicationsCustom high Gloss Extruded SheetRefrigeration accessoriesSmall Appliances.. |
|||
| Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
| Teknor Apex APEX® 04-A0386B-88 Polyvinyl Chloride, Flexible Notes: 105°C Insulation; RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||