Polymer Property : Tensile Strength at Break = 1750 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	12.1 MPa	1750 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible C8002 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	12.1 MPa	1750 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible SL60 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	12.1 MPa	1750 psi	Across Flow; ASTM D412
ExxonMobil Santoprene® 60ANS200 Thermoplastic Elastomer (discontinued **) A soft, translucent thermoplastic elastomer (TPE) with a relative haze of 85 to 90%. This material is shear-dependent and can be processed on conventional thermoplastics equipment for injection mold..
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D638
ExxonMobil OPTEMA™ TC 115 Molding, extrusion and compounding resin (discontinued **) OPTEMA TC 115 is an ethylene methyl acrylate copolymer, which can be used as a compatibilizer and impact modifier for engineering thermoplastics. It has been processed at temperatures up to 625°F w..
Tensile Strength at Break	12.1 MPa	1750 psi	510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible C8001 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D412
DuPont Elvax® 40L-03 Strippable Semiconductive Insulation Shield Formulation (discontinued **) Elvax® 40L-03 strippable semiconductive insulation shield.Information provided by DuPont.
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D412
DuPont Elvax® 40L-08 Strippable Semiconductive Insulation Shield Formulation (discontinued **) Elvax® 40L-08 strippable semiconductive insulation shield.Information provided by DuPont.
Tensile Strength at Break	12.1 MPa	1750 psi	Type IV specimen; ASTM D638
LyondellBasell PetrotheneÂ® NA216000 Low Density Polyethylene ApplicationsPETROTHENE NA 216-000 is a general purpose, heavy and medium weight coating resin, capable of coating weights down to 7.0 lbs/ream at line speeds of 1200 ft/min. It can be applied to pa..
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D1414
Greene Tweed CHEMRAZÂ® 505 Perfluoroelastomer ChemrazÂ® 505, a perfluoroelastomer, provides a broader range of chemical resistance than any other compound on the market. With a temperature range of -22Â°F to 446Â°F (-30Â°C to 230Â°C)..
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D1414
Greene Tweed CHEMRAZÂ® 565 Perfluoroelastomer ChemrazÂ®, a proprietary Greene, Tweed compound, has the broadest chemical resistance of any elastomeric material. Chemraz combines the resilience and sealing force of an elastomer with chemical r..
Tensile Strength at Break	12.1 - 13.8 MPa	1750 - 2000 psi
ITW Plexus Plexusâ„¢ MA1020 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Low shrinkage, low odor, all purpose.Information provided by Illinois Tool Works.
Tensile Strength at Break	12.1 - 13.8 MPa	1750 - 2000 psi
ITW Plexus Plexusâ„¢ MA1023 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Low shrinkage, low odor, all purpose.Information provided by Illinois Tool Works.
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D1414
Greene Tweed CHEMRAZÂ® 550 Perfluoroelastomer Chemraz Â® 550 is recommended for use in wet systems where chemical compatibility is required and small amounts of contamination are acceptable. This seal material has a wide variety of uses in d..
Tensile Strength at Break	12.1 - 13.8 MPa	1750 - 2000 psi
ITW Plexus Plexusâ„¢ MA1025 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Low shrinkage, low odor, able to be used 1" thick.Information provided by Illinois Tool Works.
Tensile Strength at Break	12.1 - 13.8 MPa	1750 - 2000 psi
ITW Plexus Plexusâ„¢ MA550 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Excellent marine adhesive, UV stable.Information provided by Illinois Tool Works.
Tensile Strength at Break	12.1 MPa	1750 psi	ISO R 527
Stir SpA AF 77 CZ (PVC) Application: Extrusion flame resistant sheath CEI 20-11 type TM 2Information provided by STIR SpA
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D638
Teknor Apex APEXÂ® 90-A471R-6-NT Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Radiation (Gamma) Resistant; Radiation Sterilizable Uses: Medical/Healthcare Applications; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Tekno..
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D412
Teknor Apex MonpreneÂ® MP 1097F Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D412
Teknor Apex Telcar® TL-81-D965-P Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets ..
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D412
Teknor Apex Telcar® TL-8732 Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets ..
Tensile Strength at Break	12.1 MPa	1750 psi	Forming
LG Chemical NBR 8300 High Acrylonitrile Polymer Description: NBR 8300 is a copolymer of butadiene-acrylonitrile and the powdered nitrile elastomer manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 8300 has ..
Tensile Strength at Break	12.1 MPa	1750 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FC 2161X Fluoroelastomer (discontinued **) Composition: di-polymer of vinylidene fluoride and hexafluoropropyleneMedium viscosityProcess targets: compression and transfer molding, and calenderingProprietary incorporated cure technologyExcell..