Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | ASTM D412 |
Parker Chomerics CHO-SEAL 1356 Conductive Elastomer Commercial Grade Conductive Elastomer Extrusions. These materials offer excellent cost/performance characteristics for commercial EMI gasket applications. These silicone and fluorosilicone based con.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | ASTM D412 |
Parker Chomerics CHO-SEAL® 6310 Extruded Elastomer Low Cost Commercial Grade Extruded Elastomer. CHO-SEAL 6310 is the latest addition to Chomerics line of low cost, commercial grade EMI gaskets. This extruded material combines nickel-plated graphite.. |
|||
Tensile Strength at Break | 0.689 MPa | 100 psi | |
Shin-Etsu Silicones KE-3421 Silicone, RTV Conformal Coating Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
Tensile Strength at Break | 0.689 MPa | 100 psi | |
Shin-Etsu Silicones KE-3472T Silicone, RTV Conformal Coating Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
Tensile Strength at Break | 0.689 MPa | 100 psi | ASTM D412 |
Teknor Apex Monprene® MP-2137 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A |
ExxonMobil Escorene™ FL 00212 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00212 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 260°C (500°F) may cause resin degradation. Machines should always b.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ FL 00309 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00309 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 270°C (513°F) may cause resin degradation. Availability: Africa & M.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ FL 00623 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00623 is a good coextrusion partner in extrusion coating, blown and cast film. Excellent sealing material with a very low seal initiation temperature. Availability: Africa & .. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ FL 00714 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00714 is an easy processable grade for extrusion coating, co-extrusion coating and cast film. This grade offers excellent heat sealing characteristics and excellent optical p.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ FL 00728CC Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00728CC is an excellent coextrusion partner in extrusion coating, blown and cast film. Good adhesion onto OPP in coextrusion. This grade offers excellent optical, low gel and.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ FL 00909 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00909 is used in extrusion coating, cast film and co-extrusion. FL 00909 is good sealing material with good optical properties.Processing Conditions: Excellent results are ob.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ FL 02020 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 02020 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. FL 02020 is an excellent sealing materi.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ UL 00218CC3 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00218CC3 is a copolymer of ethylene and vinyl acetate.Processing Conditions: Processing temperature above 240°C (464°F) may cause resin degradation.Availability: Africa & M.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ UL 00226CC Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00226CC is a copolymer of ethylene and vinyl acetate.Processing Conditions: Processing temperature above 230°C (446°F) may cause resin degradation.Availability: Africa & Mi.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A |
ExxonMobil Escorene™ UL 00328 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00328 is a copolymer of ethylene and vinyl acetate.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: No Applications: Compoun.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A |
ExxonMobil Escorene™ UL 00514 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00514 is a copolymer of ethylene and vinyl acetate.Processing Conditions: Processing temperatures above 250°C (482°F) may cause resin degradation.Availability: Africa & Mid.. |
|||
Tensile Strength at Break | 0.689 MPa | 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ UL 00728 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00728 is a copolymer of ethylene and vinyl acetate.Processing Conditions: Processing temperatures above 220°C (428°F) may cause resin degradation.Availability: Africa & Mid.. |
|||
Tensile Strength at Break | 0.689 MPa | 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ UL 00728CC Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00728CC is a copolymer of ethylene and vinyl acetate.Processing Conditions: Processing temperatures above 220°C (428°F) may cause resin degradation.Availability: Africa & M.. |
|||
Tensile Strength at Break | 0.689 MPa | 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ UL 00728FF Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00728 is a copolymer of ethylene and vinyl acetate.Processing Conditions: Processing temperatures above 220°C (428°F) may cause resin degradation.Availability: Africa & Mid.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ UL 02020 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 02020 is a copolymer of ethylene and vinyl acetate.Processing Conditions: Processing temperatures above 240°C (464°F) may cause resin degradation.Availability: Africa & Mid.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A |
ExxonMobil Escorene™ FL 00206 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00206 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 280°C (536°F) may cause resin degradation. Machines should always b.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ FL 00226CC Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00226CC is a copolymer of ethylene and vinyl acetate offering low gel. Processing Conditions: Processing temperatures above 230°C (446°F) may cause resin degradation. Machi.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A |
ExxonMobil Escorene™ FL 01418 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 01418 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. FL 01418 is an excellent sealing materi.. |
|||
Tensile Strength at Break | 0.690 MPa | 100 psi | ASTM D3574 |
3M 4508 Foam Tape Use these tapes to protect products from the elements of destruction. Two different backing/adhesive combinations meet demanding applications requiring gasketing, baffling, cushioning, and insulatio.. |
|||
Tensile Strength at Break | 0.690 MPa | 100 psi | T-Block on Aluminum; ASTM D987 |
3M VHB™ F9460PC Adhesive Transfer Tapes with Adhesive 100MP 3M™ VHB™ Adhesive Transfer Tapes F9460PC, F9469PC and F9473PC utilize the 3M™ High Performance Acrylic Adhesive 100MP, which has excellent long term holding power with much higher adhesion streng.. |
|||
Tensile Strength at Break | 0.690 MPa | 100 psi | T-Block on Aluminum; ASTM D987 |
3M VHB™ F9469PC Adhesive Transfer Tapes with Adhesive 100MP 3M™ VHB™ Adhesive Transfer Tapes F9460PC, F9469PC and F9473PC utilize the 3M™ High Performance Acrylic Adhesive 100MP, which has excellent long term holding power with much higher adhesion streng.. |
|||
Tensile Strength at Break | 0.690 MPa | 100 psi | T-Block on Aluminum; ASTM D987 |
3M VHB™ F9473PC Adhesive Transfer Tapes with Adhesive 100MP 3M™ VHB™ Adhesive Transfer Tapes F9460PC, F9469PC and F9473PC utilize the 3M™ High Performance Acrylic Adhesive 100MP, which has excellent long term holding power with much higher adhesion streng.. |
|||
Tensile Strength at Break | 0.690 MPa | 100 psi | Die "A"; ASTM D3759 |
3M 4508 Single-Coated Foam Tape 3M™ Single-Coated Foam Tapes will adhere to a variety of substrates, including latex-painted wood, lacquered wood, enameled steel, glass, aluminum, stainless steel, acrylic, ABS, and PVC (non-plast.. |
|||
Tensile Strength at Break | >= 0.689 MPa | >= 100 psi | Molded Properties; ISO 527-2/1A/100 |
ExxonMobil Escorene™ FL 00328 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00328 is a copolymer of ethylene and vinyl acetate offering low gel. Processing Conditions: Processing temperatures above 220°C (428°F) may cause resin degradation. Machine.. |