Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 89.6 MPa | 13000 psi | 2 in/min; ASTM D638 |
RheTech Products GC30P101-00 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Natural Applications: BracketsHead lamp housingsBattery trayFan shroudInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | 2 in/min; ASTM D638 |
RheTech Products GC43P250-777 43% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Ivory Applications: BracketsStructural supportsDurable GoodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Niche Polymer PPHG30BK Homopolymer PP, 30% Glass Fiber Filled Information provided by Niche Polymer |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Polymer Resources NY66-GP2-[color]-H General Purpose Nylon 66, Nucleated, Heat Stabilized General Purpose Nylon 66, Nucleated, Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grade.. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Polymer Resources NY6-GP2 General Purpose Nylon 6, Nucleated General Purpose Nylon 6, Nucleated Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry .. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Polymer Resources PC/TP-GP3-G30 PC/Polyester Alloy, 30% Glass Reinforced Superior Chemical Resistance, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Polymer Resources NY66-GP2 General Purpose Nylon 66, Nucleated General Purpose Nylon 66, Nucleated Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry.. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Polymer Resources NY6-GP2-[color]-H General Purpose Nylon 6, Nucleated, Heat Stabilized General Purpose Nylon 6, Nucleated, Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades.. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Polymer Resources NY6-M40 Nylon 6, 40% Mineral Filled Nylon 6, 40% Mineral Filled, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested .. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Ravago Manufacturing Americas Enviramid™ N1335STHL BK Post Consumer Recycle Nylon 66, 35% Glass Filled Superior Toughness, Heat Stabilized, Lubricated, Black and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Techmer ES Electrafil® NY-3/EC BK PA6 |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
Chase Plastics CP Pryme® N310GL (DAM) Nylon 6 (Utility Grade), 10% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 89.6 MPa | 13000 psi | 2 in/min; ASTM D638 |
RheTech Products GC43P250-01 43% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black Applications: Consumer goodsFunctional supportsHead lamp bracketsDurable GoodsInjection molding conditions reported in table.Information provided by RheTech Products. |