- Polymer Property : Tensile Strength at Break = 75.8 MPa
Polymer Property : Tensile Strength at Break = 75.8 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.8 MPa | 11000 psi | 2 in/min; ASTM D638 |
| RheTech Products F55-01 43% Glass Fiber/Talc Co-Reinforced Polypropylene Copolymer, Chemically Coupled, Black Applications: Consumer goodsSupportsGolf cart bracketsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Tensile Strength at Break | 75.8 MPa | 11000 psi | Type I, 5.1 mm/min; ASTM D638 |
| PolyOne Nymax™ 623 HS Black 13 1 Polyamide 6 Alloy (Nylon 6 Alloy) The Nymax® 600 Blend Series of nylon 6 materials are salt-and-pepper pelletized blends combining select nylon resins and process aids, performance modifiers, and color concentrates. These materials.. |
|||
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ASTM D638 |
| Polymer Resources NY6-GP1 General Purpose Nylon 6 General Purpose Nylon 6, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry .. |
|||
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ASTM D638 |
| Polymer Resources NY6-GP1-[color]H Nylon, General Purpose, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Tensile Strength at Break | 75.8 MPa | 11000 psi | 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA), 33% Glass Fiber Amodel® AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e.. |
|||
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ASTM D638 |
| Techmer ES Plaslube® J-1/AF/15/TF/10 NAT PA66 |
|||
| Tensile Strength at Break | 75.8 MPa | 11000 psi | ASTM D638 |
| A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66 Information provided by A. Schulman. |
|||