Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 72.4 MPa | 10500 psi | 2 in/min; ASTM D638 |
RheTech Products F56-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black Applications: Consumer goodsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 2 in/min; ASTM D638 |
RheTech Products GC20P200-00 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Natural Applications: Consumer goodsBoat handlesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 2 in/min; ASTM D638 |
RheTech Products GC30P100-01UV 30% Glass Fiber Reinforced Polypropylene, Chemically Coupled, UV Stabilized, Black Applications: Exterior automotive componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Network Polymers Nylon 6001 L Description: General Purpose Black NylonInformation provided by Network Polymers Inc. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Oxford Polymers ABS 30GF-BK ABS, 30% Glass Fiber Reinforced Product Description: Glass Fiber (30% Reinforced), ABS injection molding grade Processing and Delivery Form: Pellets and Injection Molding Additives: Release AgentsSpecial Characteristics: Pre-colo.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Polymer Resources PC-GP1-D Polycarbonate, General Purpose, Low Flow Polycarbonate, General Purpose, Low FlowFeatures: • Ultra High Impact Resistance • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Polymer Resources PC-GP1-D-[color]-5 Polycarbonate, FDA-compliant Feedstocks, Low Flow Polycarbonate, FDA-compliant Feedstocks, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pro.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Polymer Resources TP-GFMF2 Polybutylene Terephthalate, 40% Glass/Mineral Reinforced Polybutylene Terephthalate, 40% Glass/Mineral ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informat.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N1000NL2 Nylon 6/6 (Cond) Information provided by Ravago. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Techmer ES Electrafil® NY-7/EC NAT PA6 |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 200-3 Polycarbonate Resin Overview: CALIBREâ„¢ 200-3 polycarbonate resin is produced in compliance with the US Food and Drugs Administration (FDA) and EU food contact regulation. This resin provides excellent impact resis.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 300-6 Polycarbonate Resin Overview: CALIBREâ„¢ 300-6 polycarbonate resin offer exceptional impact resistance, heat distortion resistance, and optical clarity as high melt strength for blow molding and sheet applications. .. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 302-6 Polycarbonate Resin Overview: CALIBREâ„¢ 300-6 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, and optical clarity as well as high melt strength for blow molding and sheet appli.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 302V-6 LD Polycarbonate Resin Overview: CALIBREâ„¢ 302V-6 LD HC18010009 Polycarbonate is an opalescent white extrusion-grade resin containing a proprietary light diffusion package that offers an excellent combination of light.. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | 50 mm/min; ASTM D638 |
Styron CALIBREâ„¢ 303V-6 Polycarbonate Resin Overview: CALIBREâ„¢ 303V-6 Polycarbonate resins offer exceptional impact resistance and heat distortion resistance, and meets UL94 V-2 rating. CALIBRE 303V-6 contains a mold release agent, a UV .. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
Chase Plastics CP Pryme® A120 ABS, 20% Glass Fiber Reinforced Features: Glass fiber reinforcementInjection moldingForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D882 |
Westlake Plastics PES film Made from ULTRASON® E Polyethersulfone Resin High heat deflection and continuous use temperature. Exceptional tensile and flexural strength. High dielectric strength. Exceptional mechanical properties. Dimensionally stable at varying tempera.. |