Polymer Property : Tensile Strength at Break = 26.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products CC30P100-01 30% Calcium Carbonate Reinforced Polypropylene, Black Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products FRp256-01 Polypropylene Copolymer, Flame Retardant, Black Applications: Electrical component housingsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products FRP300-00 20% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Natural Applications: Electrical component housingsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products P252-01 Polypropylene Copolymer, Black Applications: Cowl screenInterior trimBumper coverGlove box binInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products RCT220-01 20% Talc Reinforced Polypropylene Copolymer, Black, Recycled Content Applications: Fan shroudsElectrical housingsHush panelsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products T20P252-00 20% Talc Reinforced Polypropylene, Natural Applications: IP Structural componentsGlove box binWire troughInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products T20P252-01 20% Talc Reinforced Polypropylene Copolymer, Black Applications: IP Structural componentsGlove box binWire troughInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	26.2 MPa	3800 psi	chs 2 in/min; ASTM D638
Network Polymers NPS 80-1410 Polystyrene Description: Injection Molding Grade, Medium Impact, High Melt FlowInformation provided by Network Polymers Inc.
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
Ineos H44N-00 Polypropylene Homopolymer H44N-00 is a high flow rate, nucleated polypropylene homopolymer designed for compounding and injection molding applications. The grade benefits from a high stiffness and isotropic shrinkage to help..
Tensile Strength at Break	26.2 MPa	3800 psi	additive of steel and GRAFOILÂ® flexible graphite
GrafTech GRAFOILÂ® GHR Standard Fluid Sealing Laminate, Metal Reinforced GRAFOILÂ® Grade GHR is an uncured laminate made with GRAFOILÂ® Grade GTB flexible graphite adhesively bonded to both faces of a 0.002" thick flat 316 or 316L stainless steel insert. Surface iden..
Tensile Strength at Break	26.2 MPa	3800 psi	ASTM D638
Teknor Apex Synres® SR 1288A Polypropylene Notes: The Specialty Compounding Division offers a proprietary line of mineral filled polyolefins, including talc and calcium carbonate filled polypropylenes. Typical applications include injection ..
Tensile Strength at Break	26.2 MPa	3800 psi	ASTM D412
Teknor Apex Telcar® TL-2683A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets ..
Tensile Strength at Break	26.2 MPa	3800 psi	ASTM D638
Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10-15 mils) per coat..
Tensile Strength at Break	26.2 MPa	3800 psi	ASTM D638
Chesterton MRS SD4i Metal Rebuilding System An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10 – 15 mils) per coat. Non-shri..
Tensile Strength at Break	26.2 MPa	3800 psi	vs. rigid PVC; 10 s set time
Elmer's Products Aron Alpha® 432TW Cyanoacrylate Adhesive (Industrial Krazy Glue™) Extra tough adhesives with highest heat, peeling, impact and thermal shock resistance.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Excellent on metal substrates. Fa..
Tensile Strength at Break	26.2 MPa	3800 psi	vs. aluminum; 15 s set time
Elmer's Products Aron Alpha® 802 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Low odor, low chlorosis (bloom) when a transparent bond, appearance and strength are required.Medium gap fill. Ethoxyethyl monomer. Excellent on rubber/plastic substrates. Fair on metal substrate..
Tensile Strength at Break	26.2 MPa	3800 psi	vs. aluminum; 30 s set time
Elmer's Products Aron Alpha® 803 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Low odor, low chlorosis (bloom) when a transparent bond, appearance and strength are required.High gap fill. Ethoxyethyl monomer. Excellent on rubber/plastic substrates. Fair on metal substrates...
Tensile Strength at Break	26.2 MPa	3800 psi	vs. rigid PVC; 5 s set time
Elmer's Products Aron Alpha® GEL 10 Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break	26.2 MPa	3800 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DMDB-7950 NT 7 High Density Polyethylene Resin DOW DMDB-7950 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as roll-out trash carts and other large parts with short mo..
Tensile Strength at Break	26.2 MPa	3800 psi	ASTM D882
3M 15CV826 General Purpose Temporary Surface Protection Tape 3M™ General Purpose Temporary Surface Protection Tape 15CV826 is a medium adhesion temporary protection tape designed for a variety of surface protection applications.Information provided by 3M
Tensile Strength at Break	26.2 MPa	3800 psi
Abatron AboCast 8501-6 One-Component Epoxy AboCast 8501-6 is a clear, high-temperature one-component epoxy system for very high-temperature uses. It offers the highest heat resistance of the clear resins. Suggested Uses: Casting; Potting; E..
Tensile Strength at Break	26.2 MPa	3800 psi	TM R050-36
Resinlab® EP1300 Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Black (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and ..
Tensile Strength at Break	26.2 MPa	3800 psi	TM R050-36
Resinlab® EP1300 Clear Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Clear (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and ..
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products CC30P100-00 30% Calcium Carbonate Reinforced Polypropylene, Natural Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	26.2 MPa	3800 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Stat-Tech™ PP-CP1/000 HF6 Black Polypropylene Impact Copolymer (PP Impact Copolymer) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Tensile Strength at Break	26.2 MPa	3800 psi	2 in/min; ASTM D638
RheTech Products HP507-01 38% Talc Reinforced High Performance Polypropylene, Non-UV Stabilized, Black Applications: IP structural componentsSpeaker housingsAutomotive interior componentsInjection molding conditions reported in table.Information provided by RheTech Products.