Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 115 MPa | 16700 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® BKV 140 H2.0 900051 Copolyamide, 40% Glass Fiber CoPA, injection molding grade, 40% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 40, even in.. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527 Type 1A |
Solvay TECHNYLSTARâ„¢ S 218 V35 PA6, 35% glass filled, Conditioned Description: TECHNYL STAR Polyamide, reinforced with 35% of glass fiber, heat stabilized, for injection molding. Characterized by a high fluidity of the melt. Available in: Europe and North America .. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT (Asia Pacific) LNP* LUBRICOMP* WFL34H is a compound based on Polybutylene Terephalate resin containing PTFE, Glass Fiber. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS (Asia Pacific) LNP* Lubricomp* ZFG26 is a compound based on PPE+PS Blend resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU2110 PEI 10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP .. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 8032UX PBT+PET VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin.. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON MV007SU PP (Europe-Africa-Middle East) LNP* VERTON * MV007SU is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilizedl. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON MV007SUP PP (Europe-Africa-Middle East) LNP* VERTON* MV007SUP is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl GFN1430V PPE+PS Noryl* GFN1430V PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability. This grade has been developed for potable.. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 10 mm/min; SABIC - Japan Method |
SABIC Innovative Plastics NORYL PCN2910 PPE+PS (Asia Pacific) 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RFZ22S PA 66 LNP* THERMOCOMP* RFZ22S is a compound based on Nylon 66 resin containing 10% Glass Fiber, 10% Milled Glass. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RFZ22S PA 66 (Asia Pacific) LNP* Thermocomp* RFZ22S is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl GFN1430V PPE+PS (Asia Pacific) Noryl* GFN1430V PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability. This grade has been developed for potable.. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-2 |
Tisan TISLAMID® 6 15% Glass Fiber Reinforced Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-93 |
Wellman Wellamid® FRGF25-66 NBK3 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-93 |
Wellman Wellamid® MRGF25/15 42H-BKDX9 Nylon 6, 25% Mineral and 15% Glass Fiber Reinforced Chrysler DX9 color matchedAll information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | dry; ISO 527 |
Ter Hell Plastic Terez® PBT 7100 GF 30 Polybutylene Terephthalate, 30% Glass Fiber Description: PBT, 30% glass fiber reinforced.Application: Suitable for injection molding applications.Information provided by Ter Hell Plastic GMBH. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-1/-2 |
DSM Stanyl® 46HF4130 (COND) Nylon 46 30% Glass Reinforced, Heat Stabilized, High Flow (North America) Information provided by DSM Engineering Plastics. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527 |
Eurotec® Tecoform® PO30 GR20 NL HS POM, 20% glass fiber reinforced, heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-1 |
Barlog Plastics KEBAFORM C 2027 POM Copolymer, 20% glass fiber reinforced POM-GF20Information provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | 5 [mm/min]; ISO 527-1/2 |
Akro-Plastic Akromid® A3 GF 25 (2420) PA 6.6 Conditioned, 25% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R513H Black Nylon 66, 13% Glass Reinforced, DAM Vydyne® R513H Black is general-purpose, 13% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is an injection-molding grade that is lubricated for machine feed, flow, and m.. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R513H Nylon 66, 13% Glass Filled, Dry as Molded Vydyne® R513H is general-purpose, 13% glass-reinforced, heat stabilized PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow, and mold .. |
|||
Tensile Strength at Break | 115 MPa | 16700 psi | 0.2 in/min; ASTM Test |
BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties in.. |