Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Solvay Specialty Polymers Ryton® R-4-230NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-230NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compare.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Solvay Specialty Polymers Ryton® R-4-230BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-230BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compared to oth.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Solvay Specialty Polymers Ryton® R-4 Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4 is a 40% fiberglass reinforced polyphenylene sulfide compound which provides outstanding chemical resistance and mechanical properties even at.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Solvay Specialty Polymers Ryton® R-4 02 Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4 02 is a 40% fiberglass reinforced polyphenylene sulfide compound which provides outstanding chemical resistance and mechanical properties even at elev.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Solvay Specialty Polymers Ryton® R-7-120NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-7-120NA is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good weldline strength and low maintenance moldi.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Solvay Specialty Polymers Ryton® R-7-120BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-7-120BL is an advanced glass/mineral filled polyphenylene sulfide compound developed to provide good weldline strength and low maintenance molding using.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Chevron Phillips Ryton® R10-110BL Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® R10-110BL is a glass and mineral filled polyphenylene sulfide compound which provides a good combination of mechanical and electrical properties.Applicati.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Chevron Phillips Ryton® R-7 Polyphenylene Sulfide Compound
(discontinued **) Natural Color Polyphenylene Sulfide CompoundRyton® R-7 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compoun.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | 0° |
Hexcel® HexPly® ES 84 120°C Curing Epoxy Matrix, Aramid Balanced fabric 175 g/m2 Information provided by HexCel |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | Compression After Impact @ 6.6 J/mm, Results normalized to 60% fibre volume for Carbon, 50% fibre volume for Kevlar; pr EN 6038 |
Hexcel® HexPly® 920CX-FM40J-6-42% 125°C Curing Epoxy Matrix High modulus carbon, Unidirectional, 165 g/m2Information provided by HexCel |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | 10% Strain; EN ISO 604 |
Ensinger TECASINT 1011 Polyimide (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Compressive Yield Strength | 240 MPa | 34800 psi | ASTM D695 |
Chevron Phillips Ryton® R-7 02 Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® R-7 02 is polyphenylene sulfide compounded with glass fibers and mineral fibers to produce an injection moldable high temperature engineering compound wit.. |