Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695-69 |
Budd DSM-971 Smooth Surface, Class "A" SMC
(discontinued **) Parts requiring high strength and dimensional stability, excellent surface smoothness without sink marks; parts to be painted requiring an automotive-type finish.Data provided by the manufacturer. |
|||
Compressive Yield Strength | 145 - 221 MPa | 21000 - 32100 psi | Average value: 195 MPa Grade Count:12 |
Overview of materials for Phenolic, Novolac, Heat Resistant Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Heat Resistant Grade, Filled". Each property range of values reported is minimum and .. |
|||
Compressive Yield Strength | 145 - 276 MPa | 21000 - 40000 psi | Average value: 211 MPa Grade Count:10 |
Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
Sumitomo Bakelite North America 51-01 CAFR-P Mineral Filled Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bak North Americ.. |
|||
Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
Sumitomo Bakelite North America 775 CAF Mineral Filled Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bak North Americ.. |
|||
Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
Sumitomo Bakelite North America RX® 2-501N Mineral Filled Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Conforms with the requirements of ASTM D5948.. |
|||
Compressive Yield Strength | 145 MPa | 21000 psi | DIN EN ISO 604 |
Wolf Kunststoff ZEDEX® ZX-324V1T A3H PEEK Polymer, Reinforced Main Characteristics: High resilience; High elasticity; Low permanent deformation; Stress resistant; High strength at temperatures above 140 ° CApplications: Shipbuilding; Chemical Engineering; Aut.. |
|||
Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
Adell BJ-37 Nylon 6, 35% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 145 - 152 MPa | 21000 - 22000 psi | Average value: 148 MPa Grade Count:4 |
Overview of materials for Polycarbonate, 40% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
Sumitomo Bakelite North America FS-6 CAF Mineral Filled Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type MI.. |
|||
Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
Adell BJ-17 Nylon 6, 35% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
Adell WL-38 40% Glass and Mineral Reinforced PET |
|||
Compressive Yield Strength | 145 - 276 MPa | 21000 - 40000 psi | Average value: 185 MPa Grade Count:14 |
Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are.. |