Sumitomo Bakelite North America 775 CAF Mineral Filled Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Cast, Mineral Filler , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America 775 CAF Mineral Filled Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | |
| Water Absorption | 0.65 % | 0.65 % | 48 hours, 50°C. ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | Compression Molding. ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.0 µm/m-°C @Temperature 20.0 °C |
18.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ASTM D648A |
| Oxygen Index | 24 % | 24 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.5 @Frequency 1e+6 Hz |
4.5 @Frequency 1e+6 Hz |
Wet |
| 4.7 @Frequency 1000 Hz |
4.7 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | Wet, step-by-step. ASTM D149 |
| 17.0 kV/mm | 432 kV/in | Wet, short term. ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
Wet; ASTM D150 |
| 0.025 @Frequency 1e+6 Hz |
0.025 @Frequency 1e+6 Hz |
Wet; ASTM D150 | |
| Arc Resistance | 138 sec | 138 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL746A, ASTM D3638 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |
Users viewing this material also viewed the following:
- Proto3000 Duraform® PA Selective Laser Sintering (SLS®) Prototyping Polymer
- Raschig Group 3536 Epoxy
- PTS PBT-15GF 15% Glass Filled PBT
- Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact
- SABIC Innovative Plastics NORYL PX500 PPE (Asia Pacific)
- Schott G018-117 Dental Glass
- 3M 8911 Polyester Tape
- Asahi Glass Fluon® P-805UP PFA Perfluoropolymer
- Unifrax Fiberfrax® Bulk 8000 AZS High-Temperature Fiber
- HP Alloys Nitronic® 50 Austenitic Stainless, Level 5 Cold Worked
Copyright © lookpolymers.com All Rights Reserved