Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 132 GPa @Temperature 1093 °C |
19100 ksi @Temperature 1999 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 132 GPa @Temperature 900 °C |
19100 ksi @Temperature 1650 °F |
|
Special Metals NIMONIC® alloy 91 Ni-Cr-Co Alloy NIMONIC® alloy 91 is a wrought nickel-chromium-cobalt based alloy strengthened by additions of aluminum and titanium.This alloy is a modification of NIMONIC alloy 90, but has an increased chromium .. |