Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Adhesive Bond Strength | 0.690 - 35.0 MPa | 100 - 5080 psi | Average value: 15.7 MPa Grade Count:238 |
Overview of materials for Cyanoacrylate Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Cyanoacrylate Adhesive". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Adhesive Bond Strength | 0.690 MPa | 100 psi | ABS, Substrate Failure, Shear; ASTM D1002 |
Permabond 930 Cyanoacrylate PERMABOND 930 is a low odor, nonfogging, nonfrosting cyanoacrylate. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesives on hot and humid days, is eliminated. The .. |
|||
Adhesive Bond Strength | 0.690 MPa | 100 psi | ABS, Substrate Failure, Shear; ASTM D1002 |
Permabond 931 Cyanoacrylate PERMABOND 931 is a low odor, nonfogging, nonfrosting cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesiv.. |
|||
Adhesive Bond Strength | 0.690 MPa | 100 psi | ABS, Substrate Failure, Shear; ASTM D1002 |
Permabond 932 Cyanoacrylate PERMABOND 932 is a low odor, nonfogging, nonfrosting cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesiv.. |
|||
Adhesive Bond Strength | 0.690 MPa | 100 psi | ABS, Substrate Failure, Shear; ASTM D1002 |
Permabond 935 Cyanoacrylate The PERMABOND 930 series is a family of low odor, non-fogging, non-frosting cyanoacrylates. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyano.. |
|||
Adhesive Bond Strength | 0.690 MPa | 100 psi | Typical lap shear |
Momentive Performance Materials RTV160 White Adhesive Sealant, Non-Corrosive Pourable One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Non-corrosive prote.. |