Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Fatigue Strength | 400 MPa @# of Cycles 100000 |
58000 psi @# of Cycles 100000 |
R=-1, Kt=1 |
Materion AMC225XE T4 Aluminum/Silicon Carbide MMC Extruded Bar Aluminium alloy 2124 reinforced with 25 volume % silicon carbide particles (average size 3 micron). It is manufactured by a powder metallurgy route using high-energy mixing to ensure excellent part.. |
|||
Fatigue Strength | <= 400 MPa @# of Cycles 1.00e+6 |
<= 58000 psi @# of Cycles 1.00e+6 |
after 2% elongation and heat treatment |
ArcelorMittal 260 BH Bake hardening steel, Cold rolled Available in the following: uncoated (HC260B), electroglavanized (HC260B+ZE) and Extragal®/Galvannealed (HC260BD+Z)Description: The composition and processing of these steels are designed to promot.. |
|||
Fatigue Strength | <= 400 MPa @# of Cycles 100000 |
<= 58000 psi @# of Cycles 100000 |
|
ArcelorMittal FB 450 Hot rolled ferrite-bainite steel Available in the following: uncoated (HDT450F) and Extragal® (HDT450F+Z)Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It compr.. |
|||
Fatigue Strength | <= 400 MPa @# of Cycles 100000 |
<= 58000 psi @# of Cycles 100000 |
|
ArcelorMittal HSLA 320 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S315MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |
|||
Fatigue Strength | <= 400 MPa @# of Cycles 2.00e+6 |
<= 58000 psi @# of Cycles 2.00e+6 |
|
ArcelorMittal HSLA 360 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S355MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |
|||
Fatigue Strength | <= 400 MPa @# of Cycles 1.00e+7 |
<= 58000 psi @# of Cycles 1.00e+7 |
|
ArcelorMittal HSLA 360 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S355MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |
|||
Fatigue Strength | 400 MPa @# of Cycles 1.00e+7 , Temperature 21.0 °C |
58000 psi @# of Cycles 1.00e+7 , Temperature 69.8 °F |
|
AK Steel 410 Martensitic Stainless steel AK Steel 410 provides good corrosion resistance plus high strength and hardness. It is magnetic in both annealed and hardened conditions. A wide range of properties can be developed with different.. |