- Polymer Property : Modulus of Elasticity = 27800 ksi
Polymer Property : Modulus of Elasticity = 27800 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 315 °C |
27800 ksi @Temperature 599 °F |
|
| Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 315 °C |
27800 ksi @Temperature 599 °F |
|
| Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 500 °C |
27800 ksi @Temperature 932 °F |
|
| Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 6.4 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa | 27800 ksi | |
| Carlson 926 Mo Austenitic Stainless Steel General DescriptionCarlson alloy 926 Mo is a “super-austenitic” 6% molybdenum stainless steel that provides excellent resistance to a variety of highly corrosive environments. This alloy performs.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 400 °C |
27800 ksi @Temperature 752 °F |
|
| Assab Steels ASP 30 Cold Work Steel ASP 30 is a W-Mo-v-Co alloyed PM high speed steel characterized by:High wear resistanceHigh compressive strength at high hardnessGood through hardening propertiesGood toughnessGood dimensional stabi.. |
|||
| Modulus of Elasticity | 192 GPa | 27800 ksi | |
| ATI Allegheny Ludlum Stainless Steel Type 201, 20% Cold Work (UNS S20100) Allegheny Ludlum Type 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201 provides advantages over the 18-8 grades in certain applications. Lower cost manganese an.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 10% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||