- Polymer Property : Modulus of Elasticity = 25700 ksi
Polymer Property : Modulus of Elasticity = 25700 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 214® alloy sheet Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 214® alloy, 40% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 540 °C |
25700 ksi @Temperature 1000 °F |
|
| Haynes HR-160® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 540 °C |
25700 ksi @Temperature 1000 °F |
|
| Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 540 °C |
25700 ksi @Temperature 1000 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 540 °C |
25700 ksi @Temperature 1000 °F |
|
| Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 538 °C |
25700 ksi @Temperature 1000 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, all-weld metal, GMAW short arc HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 538 °C |
25700 ksi @Temperature 1000 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GTAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 400 °C |
25700 ksi @Temperature 752 °F |
200 HB. |
| Assab Steels 760 Machinery Steel ASSAB 760 is an easily machinable carbon steel characterized by: Good machinabilityGood mechanical strengthASSAB 760 is primarily intended to be used in the as-delivered condition. It is only to be .. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 538 °C |
25700 ksi @Temperature 1000 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 600 °C |
25700 ksi @Temperature 1110 °F |
|
| Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 538 °C |
25700 ksi @Temperature 1000 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 538 °C |
25700 ksi @Temperature 1000 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 538 °C |
25700 ksi @Temperature 1000 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 538 °C |
25700 ksi @Temperature 1000 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 177 GPa @Temperature 538 °C |
25700 ksi @Temperature 1000 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||