- HOME
- POLYMER SEARCH
- Polymer Property : Modulus of Elasticity = 170 GPa
Polymer Property : Modulus of Elasticity = 170 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 10% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 700 °C |
24700 ksi @Temperature 1290 °F |
|
| Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 538 °C |
24600 ksi @Temperature 1000 °F |
|
| Latrobe Lescalloy® Jethete M-152 ESR 2.25" RD High Strength Stainless Steel LESCALLOY JETHETE M-152 ESR is a nitrogen bearing, hardenable 12% chromium stainless steel intended for various structural components requiring high strength and good oxidation resistance up to 800Â.. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 538 °C |
24600 ksi @Temperature 1000 °F |
|
| Latrobe Lescalloy® Jethete M-152 ESR 8" RCS High Strength Stainless Steel LESCALLOY JETHETE M-152 ESR is a nitrogen bearing, hardenable 12% chromium stainless steel intended for various structural components requiring high strength and good oxidation resistance up to 800Â.. |
|||
| Modulus of Elasticity | 170 GPa | 24700 ksi | Filament property, in tension |
| Cytec Thornel® Mat VMA Carbon Fiber Data provided by the manufacturer, Amoco Performance Products, Inc.Composed of high strength, high modulus carbon filaments in a random-layered orientation. The fine diameter filaments are up to th.. |
|||
| Modulus of Elasticity | 170 GPa | 24700 ksi | Filament property, in tension |
| Cytec Thornel® Mat VMC Carbon Fiber Data provided by the manufacturer, Amoco Performance Products, Inc.Prepared by sectioning mat VMA into cubes ~ 0.5x0.5x1.0 in. VMC can be heterogeneously dispersed in matrix materials and thus enha.. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 400 °C |
24700 ksi @Temperature 752 °F |
|
| Outokumpu 725LN Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form. |
|||
| Modulus of Elasticity | 170 GPa @Temperature 538 °C |
24600 ksi @Temperature 1000 °F |
|
| Latrobe Lescalloy® Jethete M-152 ESR 6" RCS High Strength Stainless Steel LESCALLOY JETHETE M-152 ESR is a nitrogen bearing, hardenable 12% chromium stainless steel intended for various structural components requiring high strength and good oxidation resistance up to 800°.. |
|||