- Polymer Property : Modulus of Elasticity = 163 GPa
Polymer Property : Modulus of Elasticity = 163 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 705 °C |
23600 ksi @Temperature 1300 °F |
|
| Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 705 °C |
23600 ksi @Temperature 1300 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 705 °C |
23600 ksi @Temperature 1300 °F |
|
| Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
|
| Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 900 °C |
23600 ksi @Temperature 1650 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, transverse, GMAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1 H11 1/4 hard, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1C H15 Spring, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||