Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 68.0 MPa | 9860 psi | ASTM D638 |
SABIC Innovative Plastics EXTEM UH1006 TPI Blend High Heat Amorphous TPI Blend, Excellent Chemical Resistance, High Continuous Use Temperature (CUT), Best-in-class FR, OSU and LOI. Material is UL-listed. This material is RoHS compliant and also ha.. |
|||
Tensile Strength | 68.0 MPa | 9860 psi | ASTM D638 |
SABIC Innovative Plastics EXTEM UH1026 TPI Blend High heat amorphous TPI Blend, Chemical Resistant, High Flow, IR-Transparent |
|||
Tensile Strength | 68.0 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
9860 psi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded, 5.0 mm/min; ISO 527 |
PolyOne Bergamid™ B70 GK/Mi30 BK Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Tensile Strength | 68.0 MPa | 9860 psi | ASTM D638 |
Kolon SPESIN® KP513 PBT Alloy Resin Excellent extrudable and SpinningApplications: Mono filamentInformation provided by API-Kolon. |
|||
Tensile Strength | 68.0 MPa | 9860 psi | ASTM D638 |
Kolon SPESIN® KP513UG PBT Alloy Resin Extrudable, delusteringApplications: Mono filamentInformation provided by API-Kolon. |
|||
Tensile Strength | 68.0 MPa | 9860 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PA 1411 Conductive Thermoplastic Compound PRE-ELEC® PA 1411 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. PRE-ELEC® PA 1411 has a very low electrical resistivity. P.. |