Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 45.5 MPa | 6600 psi | ASTM D638 |
PolyOne Novablend™ 6602 Polyvinyl Chloride, Rigid (PVC, Rigid) Novablend 6602 is a rigid, opaque PVC for molding compounds. This product has high impact, excellent indoor/outdoor weathering, high flow, and good processing characteristics.Applications includes: .. |
|||
Tensile Strength | 45.5 MPa @Temperature 75.0 °C, Time 605000 sec |
6600 psi @Temperature 167 °F, Time 168 hour |
30 mil sheet, Immersion in Water |
Lubrizol ESTANE® 58887 Ether Based Thermoplastic Polyurethane Features: Excellent hydrolysis resistance, low temperature performance, clarity and wide processing window for extrusion.Uses: Blown and flat die/cast film extrusion, Injection and blow molding; cab.. |
|||
Tensile Strength | 45.5 MPa | 6600 psi | ASTM D412 |
Lubrizol ESTANE® 54640 Ether Based Thermoplastic Polyurethane Very good physical properties and hydrolysis resistance and wide processing window for calendering.Uses: Melt coating/calendering, flat die/cast film extrusionAvailable in Americas, Europe, Middle E.. |
|||
Tensile Strength | 45.5 MPa | 6600 psi | ASTM D638 |
Ensinger XP-154 Compression Molded PI Compound, 40% Graphite, Premium Grade The XP 150 Series are amorphous high performance polyimides with high permanent temperature and creep resistance, as well as excellent bearing and wear properties, and excellent long term thermal st.. |
|||
Tensile Strength | 45.5 MPa | 6600 psi | Cross; ASTM D882 |
Arlon CuClad 217 PTFE/Woven Fiberglass Laminate Microwave Printed Circuit Board Substrate CuClad 217 uses a low fiberglass/PTFE ratio to provide the lowest dielectric constant and dissipation factor available in fiberglass reinforced PTFE based laminates. Together, these properties offe.. |
|||
Tensile Strength | 45.5 - 59.3 MPa | 6600 - 8600 psi | |
Bulk Molding Compounds BMC T60-6002A-WG Wear Resistant Molding Compound BMC T60-6002A-WG is a wear resistant molding compound specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cost pe.. |
|||
Tensile Strength | 45.5 - 59.3 MPa | 6600 - 8600 psi | |
Bulk Molding Compounds BMC T60-6002-WG(15) Wear Resistant Molding Compound BMC T60-6002-WG-(15) is a wear resistant molding compound specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cos.. |
|||
Tensile Strength | 45.5 MPa | 6600 psi | ASTM D638 |
Aaron Industries AAROPRENE® AEN 6600-3 Nylon 6/6 Engineered Resin |
|||
Tensile Strength | 45.5 MPa | 6600 psi | ASTM D412 |
Lubrizol ESTANE® 58311 Ether Based Thermoplastic Polyurethane Features: Very good physical properties, hydrolysis resistance, low temperature performance and abrasion. Wide processing window for extrusion.Uses: Flat Die/Cast Film Extrusion, Profile ExtrusionAv.. |