Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | 42 g/10 min @Load 5.00 kg, Temperature 265 °C |
42 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® V8030CS PBT+PET Glass filled Valox with enhanced surface |
|||
Melt Index of Compound | 42 g/10 min @Load 1.20 kg, Temperature 300 °C |
42 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Melt Index of Compound | 42 g/10 min @Load 1.20 kg, Temperature 300 °C |
42 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Melt Index of Compound | 42 g/10 min @Load 1.20 kg, Temperature 300 °C |
42 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Melt Index of Compound | 42 g/10 min @Load 5.00 kg, Temperature 300 °C |
42 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ASTM D1238 |
SABIC Innovative Plastics LNP THERMOCOMP D451 PC (Asia Pacific) LNP* Thermocomp* D451 (or EXTC8141) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good duc.. |