Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 2.7 g/10 min @Load 5.00 kg |
2.7 g/10 min @Load 11.0 lb |
ISO 1133 |
Total Lacqtene® 2006 PBK 35 HDPE pipe, sheet
(discontinued **) LACQTENE® 2006 PBK 35 is a medium density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2006 PBK 35 may be used for pipe extrusion (micro-irriga.. |
|||
Melt Flow | 2.7 g/10 min @Load 5.00 kg |
2.7 g/10 min @Load 11.0 lb |
ISO 1133 |
Total Lacqtene® 2006 TN 35 HDPE pipe coating
(discontinued **) LACQTENE® 2006 TN 35 is a medium density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2006 TN 35 may be used for pipe and sheet extrusion (flex.. |
|||
Melt Flow | 2.7 g/10 min @Load 21.6 kg, Temperature 190 °C |
2.7 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
Iran Petrochemical (PCC) BL6 HM7255 High Density Polyethylene BL6 (HM 755) is a high density polyethylene with Butene-1 as a comonomer. It is a high molar mass material with very good impact strength, stiffness, and stress cracking resistance.Applications: la.. |
|||
Melt Flow | 2.7 g/10 min @Load 21.6 kg, Temperature 190 °C |
2.7 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
Iran Petrochemical (PCC) BL 3VD HH 4765 High Density Polyethylene BL3VD is a high density polyethylene with 1-Butene as co monomer. It is very high density and stiffness, good ESCR, high flowability and impact strength.Applications: small blow molding, bottles, c.. |
|||
Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Topas Advanced Polymers TOPAS® Elastomer E-140 Developmental Cyclic Olefin Copolymer (COC) TOPAS® Elastomer E-140, unlike most TOPAS grades, is a semicrystalline cyclic olefin material with flexibility. It is a fairly stiff elastomer which can be extruded and injection molded, and can be.. |
|||
Melt Flow | 2.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
Denka CL-430 Transparent Resin Polymer (MABS) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Melt Flow | 2.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
Denka TE-20 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Melt Flow | 2.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
Diamond Polymers ABS TR-7 Description: High Heat ABSInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 2.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
Diamond Polymers ASA S190 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 2.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
Diamond Polymers ASA S750 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 2.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
Diamond Polymers ASA S910 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 2.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
Diamond Polymers SE 3 HH Description: High Heat ABSInformation provided by Diamond Polymers, Inc. |