Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
SABIC F01552 High Density Polyethylene for Blown Film Product Description: F01552 is a high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weigh.. |
|||
Melt Flow | 0.15 - 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 - 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 4148B (484H2) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 0.15 - 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 - 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 6252J (526F2) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 0.15 - 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 - 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
NIZHNEKAMSKNEFTEKHIM PE 4252J (524F2) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Unipetrol PE HD LITEN® BB 29 HDPE Made for blow molding, extrusion, and pipe applications.Information provided by Unipetrol RPA |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Unipetrol PE HD LITEN® BB 85 HDPE Made for blow molding, extrusion, and pipe applications.Information provided by Unipetrol RPA |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Unipetrol PE HD LITEN® FB 29 HDPE Made for tubular film applications.Information provided by Unipetrol RPA |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Unipetrol PE HD LITEN® FB 85 HDPE Made for tubular film applications.Information provided by Unipetrol RPA |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Total MDPE HF 513 Medium Density Polyethylene, Blown Film MDPE HF 513 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HF 513 is a semi-high molecular weight polyethylene giving excellent mechanic.. |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg |
0.15 g/10 min @Load 4.76 lb |
ASTM D 1238 |
Total HT 514 MDPE film Finathene® HT 514 is a medium density polyethylene produced by the slurry loop low pressure polymerization process. Finathene® HT 514 can be used alone, blended or coextruded in a wide variety of .. |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Total MDPE HT 514 Medium Density Polyethylene, Blown Film MDPE HT 514 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HT 514 is a semi-high molecular weight polyethylene giving excellent mechanic.. |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Unipetrol PE HD LITEN® VL 20 N HDPE Made for blow molding, extrusion, and pipe applications.Information provided by Unipetrol RPA |
|||
Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Unipetrol PE HD LITEN® ZB 20 HDPE Made for blow molding, extrusion, and pipe applications.Information provided by Unipetrol RPA |