Total MDPE HF 513 Medium Density Polyethylene, Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer Total Atofina
Trade Name MDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total MDPE HF 513 Medium Density Polyethylene, Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MDPE HF 513 is a medium density polyethylene produced by slurry loop low pressure process with hexene as co-monomer.MDPE HF 513 is a semi-high molecular weight polyethylene giving excellent mechanical properties. It shows a broad molecular weight distribution ensuring outstanding processability.MDPE HF 513 can be used alone, blended or coextruded in a wide variety of blown film applications : consumer, industrial, food or hygiene packaging.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.934 g/cc
0.934 g/cc
ISO 1183
Melt Flow 0.15 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.15 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
14.5 g/10 min

@Load 21.60 kg,
Temperature 190 °C
14.5 g/10 min

@Load 47.62 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 18.0 MPa

@Thickness 0.0400 mm
2610 psi

@Thickness 0.00157 in
ISO 527-3
20.0 MPa

@Thickness 0.0200 mm
2900 psi

@Thickness 0.000787 in
ISO 527-3
Film Tensile Strength at Yield, TD 18.0 MPa

@Thickness 0.0400 mm
2610 psi

@Thickness 0.00157 in
ISO 527-3
19.0 MPa

@Thickness 0.0200 mm
2760 psi

@Thickness 0.000787 in
ISO 527-3
Film Elongation at Break, MD 400 %

@Thickness 0.0200 mm
400 %

@Thickness 0.000787 in
ISO 527-3
540 %

@Thickness 0.0400 mm
540 %

@Thickness 0.00157 in
ISO 527-3
Film Elongation at Break, TD 500 %

@Thickness 0.0200 mm
500 %

@Thickness 0.000787 in
ISO 527-3
620 %

@Thickness 0.0400 mm
620 %

@Thickness 0.00157 in
ISO 527-3
Flexural Modulus 0.620 GPa

@Strain <=0.250 %
89.9 ksi

@Strain <=0.250 %
ISO 178
Elmendorf Tear Strength, MD 1.10 g/micron

@Thickness 0.0200 mm
27.9 g/mil

@Thickness 0.000787 in
ISO 6383-1
2.40 g/micron

@Thickness 0.0400 mm
61.0 g/mil

@Thickness 0.00157 in
ISO 6383-1
Elmendorf Tear Strength, TD 13.8 g/micron

@Thickness 0.0200 mm
351 g/mil

@Thickness 0.000787 in
ISO 6383-1
18.9 g/micron

@Thickness 0.0400 mm
480 g/mil

@Thickness 0.00157 in
ISO 6383-1
Dart Drop Test 220 g

@Thickness 0.0200 mm
0.485 lb

@Thickness 0.000787 in
ISO 7765-1
290 g

@Thickness 0.0400 mm
0.639 lb

@Thickness 0.00157 in
ISO 7765-1
Film Tensile Strength at Break, MD 55.0 MPa

@Thickness 0.0400 mm
7980 psi

@Thickness 0.00157 in
ISO 527-3
65.0 MPa

@Thickness 0.0200 mm
9430 psi

@Thickness 0.000787 in
ISO 527-3
Film Tensile Strength at Break, TD 52.0 MPa

@Thickness 0.0200 mm
7540 psi

@Thickness 0.000787 in
ISO 527-3
52.0 MPa

@Thickness 0.0400 mm
7540 psi

@Thickness 0.00157 in
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 125 °C
257 °F
ISO 11357
Vicat Softening Point 118 °C
244 °F
ISO 306
Processing Properties Metric English Comments
Processing Temperature 190 - 220 °C
374 - 428 °F
Extrusion