Polymer Property : Melt Flow = 1.8 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	1.8 - 2.4 g/10 min	1.8 - 2.4 g/10 min	ASTM D1238
Plaskolite Optix® CA-81 UVA UV-Absorbing Acrylic Resin Special UV-absorption grade, extrusion and injection moldingApplications: A special UV-absorption acrylic resin for extrusion and injection molding. It is slightly lubricated for ease of processing..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	Procedure A Condition L; ASTM D1238
Network Polymers NPP 25-0216 Description: Copolymer PolypropyleneInformation provided by Network Polymers Inc.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	Condition L; ASTM D1238
PolyMirae Moplen EP340G Sheet and Thermoforming Grade Polypropylene Moplen RP340G is the polypropylene random copolymer polymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen RP340G is a random copolymer particularly suitable for..
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 200 °C	1.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D-1238
Chevron Phillips EA3350 Crystal Polystyrene (discontinued **) High heat crystal polystyrene.Applications:Medical containersBlends with clear SB-copolymersClam-shell containersBi-axially oriented sheetFeatures:High molecular weight homopolymerHigh Vicat softeni..
Melt Flow	1.8 g/10 min	1.8 g/10 min	Exxon Method
ExxonMobil Escorene® LL-3218 LLDPE/Hexene Premium Cast Stretch Film Resin, 1.2 mil (discontinued **) Data provided by the manufacturer, Exxon Chemical.A hexene copolymer LLDPE cast film resin. Films made from LL-3218 have outstanding tensile properties as well as stiffness and toughness. These su..
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 200 °C	1.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Samsung Cheil Industries Starex® SD-0150 ABS, Unreinforced (discontinued **) Amorphous Acrylonitrile Butadiene Styrene (ABS)Characteristics: General Purpose: Good Impact Strength, Chemical Resistance, ProcessabilityApplications: Household Appliances, Auto Interior Trim and P..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Sclair® 94E Butene LMDPE Film and Extrusion Resin Features: Excellent processabilityGood stiffness and strengthHigh stretchability Applications: Overwrap filmNettingBlend resinInformation provided by Nova Chemicals
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Sclair® 14B3 Butene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, good clarity, heat resistance and barrier properties.Applications: Lamination, co-extrusion.Data provided by the manufacturer.
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® NA345009 Low Density Polyethylene (Blow Molding) ApplicationsPETROTHENE NA 345-009 is a low density homopolymer resin designed for blow molding applications. Excellent clarity combined with strength and high stiffness makes NA 345-009 an ideal ch..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® NA345009 Low Density Polyethylene (Film Extrusion) ApplicationsPETROTHENE NA 345 is a series of homopolymer resins combining premium clarity with strength and stiffness. In addition, NA 345 exhibits good impact strength on both flat and creased fil..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 Â°C	1.8 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
Ineos R01A-00 Polypropylene Random Copolymer Random copolymer R01A-00 is an antistatic polypropylene produced by a unique catalyst technology. It is designed for blow molding and extrusion applications and exhibits good stiffness and improved ..
Melt Flow	1.8 - 2.0 g/10 min @Load 2.61 kg, Temperature 190 Â°C	1.8 - 2.0 g/10 min @Load 5.75 lb, Temperature 374 Â°F	ASTM D1238
LG Chemical SEETEC BF410 LDPE Characteristics: Good Processability and Excellent Optical PropertiesAdditives: Antiblocking Agent, Slip AgentApplications: Industrial Film & Food PackageCAS No. 9002-88-4Information provided by LG ..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ISO 1133
Lucite International DiakonÂ® ST35G8 Toughened Acrylic Polymer The DiakonÂ® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness. The grades in the DiakonÂ® series can be processed b..
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 200 Â°C	1.8 g/10 min @Load 11.0 lb, Temperature 392 Â°F	Condition G; ASTM D1238
Spartech Royalite R59M Hi-Impact ABS/PVC Resin Data provided by the manufacturer. A unique ABS/PVC resin that meets the flammability standards of many industries and is a cost-effective alternative to standard fire-rated ABS. High rigidity in t..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 Â°C	1.8 g/10 min @Load 4.76 lb, Temperature 374 Â°F
Silon Tabond 3045 Adhesive Resin TABOND 3045 is LLDPE modified with maleic anhydride functional groups which promote bonding with different materials like polar polymers, metals and surface treated glass.Characteristics: â€¢ Str..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis Xmod™ GB305HP High Performance 35% Glass Fiber Reinforced Xmod GB305HP is reinforced with 35% chemically coupled glass fibers and based on a specific Polymer matrix material that is bringing excellent mechanical properties (biaxial impact behavior) as well..
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 200 °C	1.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Videolar 585 Crystal Polystyrene (GPPS) High heat extrusion crystalSuperior oriented polystyrene sheetFeatures: Low melt flowHigh molecular weightApplications: Foam applications such as egg cartons, meat trays and food serviceSuperior ori..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene DescriptionPolypropylene PP 1116-01 is a molding grade copolymer polypropylene with improved low temperature toughness and good room temperature toughness. Information provided by A. Schulman.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Total PPM R020 Polypropylene, Random Copolymer for Medical Grade Polypropylene PPM R020 is a random copolymer polypropylene with a Melt Flow Index of 1.8 g/10 min specially developed for the extrusion blow molding of medical containers and medical devices, to the..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Total PPM R021 Polypropylene, Random Copolymer for Medical Grade Polypropylene PPM R021 is a random copolymer polypropylene with a Melt Flow Index of 1.8 g/10 min specially developed for the extrusion blow molding of medical containers and medical devices, to the..
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Total PPR 3221 Random Copolymer Polypropylene, Blow Molding and Sheet Extrusion Polypropylene PPR 3221 is a high clarity, high impact resistance random copolymer especially designed for blow molding applications (mono and multi-layers) for food and non-food packaging of sauces,..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene DescriptionPolypropylene PP 1116-01 is a molding grade copolymer polypropylene with improved low temperature toughness and good room temperature toughness. Information provided by A. Schulman.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Total PPH 3276 Polypropylene, Oriented Film Extrusion Grade Homopolymer film gradeLow Residuals – Fina 3276 utilizes the new Fina proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock ..
Melt Flow	1.8 g/10 min @Load 5.00 kg, Temperature 200 °C	1.8 g/10 min @Load 11.0 lb, Temperature 392 °F
BASF Polystyrol® 168 NO Polystyrene (Europe) High molecular, heat-resistant grades for the extrusion of low-taint food packaging, especially BOPS.Data was collected by ISO methods and provided by BASF.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Novapol® TF-0242-E Hexene LLDPE Film Resin (discontinued **) Excellent stiffness and glossApplications: Diaper back sheet, BlendingFilm properties are typical of film extruded at 270°C.Information provided by NOVA Chemicals.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 190 °C	1.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Novapol® TR-0242-UG MDPE Rotational Molding Resin (discontinued **) Hexene copolymer, Excellent impact, Excellent ESCRApplications: Large parts, Agricultural storage tanksAdditives: Processing antioxidants, UV stabilizersInformation provided by NOVA Chemicals.
Melt Flow	1.8 g/10 min @Load 2.16 kg, Temperature 230 °C	1.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Total PPR 3260 Random Copolymer Polypropylene, Extrusion Grade Polypropylene PPR 3260 is a random copolymer polypropylene with a melt flow index of 1.8 g/10 min suitable for extrusion applications.Information provided by Total Petrochemicals.
Melt Flow	1.8 g/10 min @Load 3.80 kg, Temperature 230 °C	1.8 g/10 min @Load 8.38 lb, Temperature 446 °F
Arkema Group Oroglas® V 045 I Acrylic, Extrusion Grade (discontinued **) OROGLAS V 045 I is an extrusion that exhibits the following properties : 50% tougher than standard acrylics excellent optical properties ( comparable to that of standard acrylics) superior surface ..
Melt Flow	1.8 g/10 min	1.8 g/10 min	Exxon Method
ExxonMobil Escorene® LL-3218 LLDPE/Hexene Premium Cast Stretch Film Resin, 0.8 mil (discontinued **) Data provided by the manufacturer, Exxon Chemical.A hexene copolymer LLDPE cast film resin. Films made from LL-3218 have outstanding tensile properties as well as stiffness and toughness. These su..
Melt Flow	1.8 g/10 min	1.8 g/10 min	ASTM D1238
Huntsman PE6021 Blow Molding Polyethylene (discontinued **) Homopolymer, Drug Master File listed product, complies with USP Classification VI, and FDA compliant.Features: Meets exacting requirements of blow molded containers and processes well with parison s..