Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 4.00 - 60.0 g/10 min | 4.00 - 60.0 g/10 min | Average value: 23.0 g/10 min Grade Count:41 |
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% .. |
|||
Melt Flow | 6.00 - 60.0 g/10 min | 6.00 - 60.0 g/10 min | Average value: 24.2 g/10 min Grade Count:13 |
Overview of materials for Polystyrene + Polyphenylene Ether, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene + Polyphenylene Ether, Unreinforced". Each property range of values reported is minimum and .. |
|||
Melt Flow | 6.00 - 60.0 g/10 min | 6.00 - 60.0 g/10 min | Average value: 15.6 g/10 min Grade Count:35 |
Overview of materials for Polycarbonate, Optical Grade This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Optical Grade". Each property range of values reported is minimum and maximum values of a.. |
|||
Melt Flow | 5.00 - 60.0 g/10 min | 5.00 - 60.0 g/10 min | Average value: 19.3 g/10 min Grade Count:15 |
Overview of materials for Polycarbonate, Carbon Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon Fiber Reinforced". Each property range of values reported is minimum and maximum v.. |
|||
Melt Flow | 1.90 - 60.0 g/10 min | 1.90 - 60.0 g/10 min | Average value: 14.5 g/10 min Grade Count:169 |
Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced". Each property range of values repor.. |
|||
Melt Flow | 0.100 - 60.0 g/10 min | 0.100 - 60.0 g/10 min | Average value: 15.7 g/10 min Grade Count:39 |
Overview of materials for Cyclo Olefin Polymer This property data is a summary of similar materials in the MatWeb database for the category "Cyclo Olefin Polymer". Each property range of values reported is minimum and maximum values of appropria.. |
|||
Melt Flow | 3.00 - 60.0 g/10 min | 3.00 - 60.0 g/10 min | Average value: 25.9 g/10 min Grade Count:10 |
Overview of materials for Nylon 6, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of a.. |
|||
Melt Flow | 1.00 - 60.0 g/10 min | 1.00 - 60.0 g/10 min | Average value: 16.8 g/10 min Grade Count:15 |
Overview of materials for Ethylene-Methyl Acrylate Copolymer, Compounding Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene-Methyl Acrylate Copolymer, Compounding Grade". Each property range of values reported is minimu.. |
|||
Melt Flow | 0.600 - 60.0 g/10 min | 0.600 - 60.0 g/10 min | Average value: 14.5 g/10 min Grade Count:107 |
Overview of materials for Polypropylene with 10% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Talc Filler". Specific grades with primary filler content between 5% and 14% are .. |
|||
Melt Flow | 0.120 - 60.0 g/10 min | 0.120 - 60.0 g/10 min | Average value: 2.02 g/10 min Grade Count:309 |
Overview of materials for Low Density Polyethylene (LDPE), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Film Grade". Each property range of values reported is minimum and maxi.. |