Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 2.5 g/10 min @Load 1.00 kg, Temperature 235 °C |
2.5 g/10 min @Load 2.20 lb, Temperature 455 °F |
ASTM D1238 |
NYCOA 1595 HS Impact Modified, Medium Viscosity Nylon 6 Resin NYCOA 1595 HS is a medium viscosity Nylon 6 resin, which offers superior flexibility and toughness in both molding and extrusion applications. Its high melt viscosity and strength provides excellent.. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Greenflex® ML 60 Ethylene Vinyl Acetate Copolymer - Injection Molding, Compounding & Extrusion Greenflex ML 60 is an ethylene vinyl acetate copolymer (EVA) for injection molding, compounding and extrusion. Items produced with Greenflex ML 60 show very high elasticity.Main Applications: Gree.. |
|||
Melt Flow | 2.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
2.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
Premix Thermoplastics PRE-ELEC® ABS 1415 Conductive Thermoplastic Compound PRE-ELEC® ABS 1415 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® ABS.. |
|||
Melt Flow | 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
Plaskolite West Optix® CP - 82 UVA General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | DIN 53735/ISO 1133 |
Ineos Nova S-7600MG Compact Polystyrene Microgranulates
(discontinued **) High impact polystyrene Microgranulates, having a diameter of 0.8 -1.0 mm, especially useful for compounding and extrusion applications. Due to the very high viscosity and the absence of weakener, .. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Eastman 1840F Polyethylene
(discontinued **) Polyethylene 1840F is a low-density formulation with no slip or antiblock. It is suggested for film applications where enhanced processability and high clarity are required. It is characterized by.. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
Huntsman PE1023 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Good draw down characteristics.Applications: Film extrusion: drum liners, hardware packaging, and refuse bags.FDA Notes: Conforms to FDA regulation 21 CFR 17.. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® NA426225 Low Density Polyethylene, Film Extrusion Grade PETROTHENE NA426 is a series of LDPE/EVA copolymer resins for high impact and clarity packaging film. These resins exhibit excellent a broad range of extrusion conditions. Well-balanced films with e.. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Multibase Multi-Flamâ„¢ 0302 PP NH Polypropylene Features:Flame RetardantHalogen Content, Low to None Forms:PelletsProcessing Methods:Injection MoldingCoextrusionExtrusionUses:TubingPipingFurnitureInformation provided by Multibase |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 400 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK) AV-742 SL30 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wea.. |
|||
Melt Flow | 2.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
Styrolution PS 641F HIPS Styrolution PS 641F is high impact polystyrene with high heat resistance.High impactHigh heat resistanceInformation provided by Styrolution |
|||
Melt Flow | 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
Styron Magnum™ 358HP ABS, High Heat MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 3063UV-3120 Black, UV Stabilized Modified Polypropylene DescriptionPolyfort® FPP 3063UV-3120 is a black, UV stabilized, 30% chemically coupled, glass reinforced, high impact resistance, modified polypropylene. Information provided by A. Schulman. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | Condition not noted.; ASTM D1238 |
DuPont Elvax® 3170SHB Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film 18 wt% Vinyl Acetate.Elvax® 3170SHB is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene res.. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 3063UV-3120 Black, UV Stabilized Modified Polypropylene DescriptionPolyfort® FPP 3063UV-3120 is a black, UV stabilized, 30% chemically coupled, glass reinforced, high impact resistance, modified polypropylene. Information provided by A. Schulman. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Westlake EF796 Low Density Polyethylene Westlake Polyethylene EF796 is a low density formulation suggested for film applications requiring a good balance of properties such as converter film for industrial packaging and general-purpose pa.. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
Westlake Elevate™ DA528AA Ethylene Vinyl Acetate Copolymer Developmental ProductDescription: Westlake ELEVATE™ DA528 is an ethylene vinyl acetate copolymer with 18.5% VA. DA528 is designed for blown and cast films requiring excellent optics and low heat s.. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Westlake EN923 Low Density Polyethylene Westlake Polyethylene EN923 is a low density formulation suggested for film applications where enhanced processability and high clarity are required. It is characterized by good tear strength, impa.. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 3063UV-3120 Black, UV Stabilized Modified Polypropylene DescriptionPolyfort® FPP 3063UV-3120 is a black, UV stabilized, 30% chemically coupled, glass reinforced, high impact resistance, modified polypropylene. Information provided by A. Schulman. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Nucrel® 903 Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film 9 wt% Methacrylic Acid.Nucrel® 0903 is an ethylene-methacrylic acid copolymer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process pol.. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polyram RamOfin PPH307G6 Polypropylene, 30% Glass Fiber 30% glass fiber reinforced, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 3063UV-3120 Black, UV Stabilized Modified Polypropylene DescriptionPolyfort® FPP 3063UV-3120 is a black, UV stabilized, 30% chemically coupled, glass reinforced, high impact resistance, modified polypropylene. Information provided by A. Schulman. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238, ISO 1133 |
DuPont™ Bynel® 41E762 Anhydride Modified LLDPE BYNEL® 41E762 is an anhydride-modified, linear low-density polyethylene (LLDPE) resin. All BYNEL Series 4100 series resins are available in pellet form for use in conventional extrusion and coextru.. |
|||
Melt Flow | 2.5 g/10 min | 2.5 g/10 min | ISO 1133 |
Domo 1102J Polypropylene Homopolymer Information provided by Domo. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg |
2.5 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 9.5. |
Dow AFFINITY™ HF 1030 Polyolefin Plastomer AFFINITY® HF 1030 polyolefin plastomer is an ethylene alpha-olefin resin designed to provide cast embossed film products with high modulus for machinability, excellent drawdown at high line speeds,.. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem Evateno® 3019 PE EVA Foam Copolymer Evateno® 3019 PE is a copolymer of Ethylene-Vinyl Acetate (EVA) with medium vinyl-acetate content. Evateno® 3019 PE is an easy processing and crosslinkable product with high compatibility with oth.. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Aaron Industries AAROPRENE® AE PC/ABS 7000-3 PC/ABS Engineered Resin Melt flow index may be specified. |
|||
Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Appeel® LSR 2044 Modified EVA Lidding Sealing Resin Appeel® 2044 is a blown or cast film resin designed to be a sealing layer for lidding applications. It provides a peelable seal over a broad temperature range to a number of container materials inc.. |