Physical Properties | Metric | English | Comments |
---|---|---|---|
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | |
Zircar Zirconia YW-15 Yttria Woven Textile Insulation Yttria (yttrium oxide - Y2O3) is typically used as a stabilizer for zirconia. It is offered here in its pure and stable metal oxide form, which is not attacked by most molten metals, including lithi.. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ISO 60 |
FKuR Kunststoff Fibrolon® P 7550 Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Fibrolon® P 7550 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C.. |
|||
Bulk Density | 0.460 - 0.540 g/cc | 0.0166 - 0.0195 lb/in³ | ASTM D1895 |
LG Chemical LS130S PVC General Description: LS130S, homopolymer made by suspension polymerization, is mainly used in PVC wire extrusion and calendar processing, well known for giving clean surfaces and bright color to the.. |
|||
Bulk Density | 0.460 - 0.540 g/cc | 0.0166 - 0.0195 lb/in³ | ASTM D1895 |
LG Chemical LS170 PVC General Description: LS170, homopolymer made by suspension polymerization, is applied for value added products such as matted sheeting, super heat resistant wire ,high pressure hose, packing and gas.. |
|||
Bulk Density | 0.460 - 0.540 g/cc | 0.0166 - 0.0195 lb/in³ | |
JPJ Technologies DG-1300 PVC Information provided by JPJ Technologies |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | |
SGL Carbon Group CF 5250 Carbon Filler Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ASTM D1895 |
Plenco 7021 Phenolic, Granular, Injection Molded PLENCO 07021 is a renumber of Plaslok 7021 which is the replacement material for the former Union Carbide BMRS-7021. It is a two-stage, impact grade phenolic molding compound suitable for compressio.. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | |
Zircar Zirconia YW-15 Yttria Woven Textile Insulation Yttria (yttrium oxide - Y2O3) is typically used as a stabilizer for zirconia. It is offered here in its pure and stable metal oxide form, which is not attacked by most molten metals, including lithi.. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ASTM D1895 |
ALM PS 200 Prototyping Polymer Non-spherical polystyrene powder for production of complex investment casting patterns.PS-200 can be used as a direct drop in replacement for Castform®, and can be successfully blended with Castfor.. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | tap; ASTM D4164 |
3D Systems CastForm™ PS Plastic for SLS® Systems For use with all selective laser sintering (SLS®) systems.ApplicationsCreate patterns directly rather than through indirect methodsComplex investment casting patternsReactive metals like titaniumLo.. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | |
Asahi Glass Fluon® G192 PTFE Granular Powder Fluon®PTFE granular powders (molding powders) are used for the production of sheets, rods, billets and other general moldings.Information provided by Asahi Glass Company, Inc. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ASTM D1895 |
ALM FR 106 Nylon 11 SLS Prototyping Polymer This flame retardant rapid prototyping material has additives in the raw material that allows it to pass aeronautic standard FAR25.853 smoke, flame, and toxicity tests. This material is ideal for Ae.. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ASTM D1895 |
ALM PA 606-FR Filled Nylon 12 Prototyping Polymer Only commercially available fire retardant nylon 12 material, which meets FAR 25.853 60 second burn specification.The parts produced from PA 606-FR have a much smoother surface finish and sharper fe.. |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ASTM D1895 |
ALM PA 620-MF Mineral Fiber Filled Nylon 12 SLS Prototyping Polymer Information provided by Advanced Laser Materials (ALM). |
|||
Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ASTM D1895 |
ALM PA 650 Nylon 12 SLS Prototyping Polymer Combines strength, durability (high impact) and chemical resistance and produces strong, durable, end use prototype parts. SL parts are less porous, more precise and have less noticeable build lines.. |