Zircar Ceramics ZAL-45AA Alumina Insulation
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Zircar Ceramics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zircar Ceramics ZAL-45AA Alumina Insulation.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ZAL-45 is an exceptionally strong low density alumina fiber product. Alumina bonded ZAL-45AA is useful in reducing conditions.Information provided by Zircar Ceramics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.720 g/cc | 0.0260 lb/in³ | |
| Open Porosity | 70 % | 70 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 6.62 MPa @Strain 7.00 % |
960 psi @Strain 7.00 % |
Load Applied Parallel to Fiber Plane, Strain = load deformation in mils for 0.5"*0.5"*4" sample |
| 6.62 MPa @Strain 13.0 % |
960 psi @Strain 13.0 % |
Load Applied Normal to Fiber Plane, Strain = load deformation in mils for 0.5"*0.5"*4" sample | |
| Compressive Yield Strength | 1.45 MPa @Strain 3.00 % |
210 psi @Strain 3.00 % |
Load Applied Normal to Fiber Plane |
| 2.62 MPa @Strain 14.0 % |
380 psi @Strain 14.0 % |
Load Applied Parallel to Fiber Plane | |
| 3.38 MPa @Strain 14.0 % |
490 psi @Strain 14.0 % |
Load Applied Normal to Fiber Plane | |
| 4.14 MPa @Strain 3.00 % |
600 psi @Strain 3.00 % |
Load Applied Parallel to Fiber Plane |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.50 µm/m-°C @Temperature 20.0 - 1000 °C |
4.17 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Specific Heat Capacity | 1.05 J/g-°C | 0.250 BTU/lb-°F | |
| Thermal Conductivity | 0.160 W/m-K @Temperature 250 °C |
1.11 BTU-in/hr-ft²-°F @Temperature 482 °F |
parallel to thickness; ASTM C177-76 |
| 0.430 W/m-K @Temperature 1650 °C |
2.98 BTU-in/hr-ft²-°F @Temperature 3000 °F |
Parallel to Thickness; ASTM C177-76 | |
| Melting Point | 1870 °C | 3400 °F | |
| Maximum Service Temperature, Air | 1550 °C | 2820 °F | Continuous |
| 1600 °C | 2910 °F | Intermittent | |
| Shrinkage | 2.00 % @Temperature 1500 °C, Time 3600 sec |
2.00 % @Temperature 2730 °F, Time 1.00 hour |
Perpendicular to Thickness |
| 6.00 % @Temperature 1600 °C, Time 3600 sec |
6.00 % @Temperature 2910 °F, Time 1.00 hour |
Perpendicular to Thickness |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 97 % | 97 % | |
| SiO2 | 3.0 % | 3.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White |
Users viewing this material also viewed the following:
- Americas Styrenics Styron® 484C High Impact Polystyrene (discontinued **)
- NOVA Chemicals Sclair® 2710 HDPE Injection Molding Resin
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N330 (HAF) Filler
- Kingfa PBT-RG152 Flame Retardant, 15% Glass Fiber Reinforced PBT
- Shandong Dongyue Polymer DF-204 PTFE Fine Powder
- Styron Pulse® 600 ABS + Polycarbonate
- SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly (Asia Pacific)
- CLAL-MSX CUPROROR® TL4 Hard, Copper Alloy
- Hexion Bakelite™ PF 4041 Phenolic Formaldehyde Resin, Resistant to High Temperatures (discontinued **)
Copyright © lookpolymers.com All Rights Reserved