Westlake Mxsite LC78105-C Polyethylene Film, Using Energx Technology Services  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Westlake Mxsite LC78105-C Polyethylene Film, Using Energx Technology Services  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Mxsite LC78105-C polyethylene is recommended for the skin layers of blown stretch film. It will provide a very aggressive cling force in both a stretched and unstretched condition. The excellent cling force comes without a substantial increase in film unwind force. It is designed for machine wrap and hand wrap applications where good processability, low gel content and substantial cling are needed. It can be used as cling layer in many "one-sided cling" films because it clings very well to many non-cling resins.Applications/UsesCast filmFilmsStretch filmEastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Base Resin Density 0.915 g/cc
0.0331 lb/in³
ASTM D1505
Thickness 20.3 microns
0.799 mil
ASTM D374
Base Resin Melt Index 0.55 g/10 min
0.55 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, TD 9.70 MPa
1410 psi
ASTM D882
Film Elongation at Break, MD 450 %
450 %
ASTM D882
Film Elongation at Break, TD 930 %
930 %
ASTM D882
Secant Modulus, MD 0.187 GPa
27.1 ksi
0.01; ASTM D882
Secant Modulus, TD 0.244 GPa
35.4 ksi
0.01; ASTM D882
Elmendorf Tear Strength, MD 18.22 g/micron
462.8 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 45.81 g/micron
1164 g/mil
ASTM D1922
Dart Drop 7.88 g/micron
200 g/mil
ASTM D1709A
Film Tensile Strength at Break, MD 39.0 MPa
5660 psi
ASTM D882
Film Tensile Strength at Break, TD 36.0 MPa
5220 psi
ASTM D882
Optical Properties Metric English Comments
Haze 3.3 %
3.3 %
ASTM D1003
Gloss 83 %
83 %
at 45°; ASTM D2457
Descriptive Properties Value Comments
Peel Cling, Aged 2 Weeks, 0% 360 g
Peel Cling, Aged 2 Weeks, 200% 260 g