Washington Penn High Modulus Polypropylene Homopolymer 40% Glass/Mica Filled

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Washington Penn
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Washington Penn High Modulus Polypropylene Homopolymer 40% Glass/Mica Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Mica-filled polypropylene compounds provide the best strength and modulus of any of the particulate fillers which results in an outstanding balance of properties. Mold shrinkage is similar to ABS and parts run in ABS tooling may be useable in size and fit. Compounds may also be supplied with very high rigidity and heat deflection temperatures.Information provided by Washington Penn Plastic Co.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Filler Content 40 %
40 %
Melt Flow 14 g/10 min
14 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 86.2 MPa
12500 psi
ASTM D638
Elongation at Break 6.6 %
6.6 %
ASTM D638
Elongation at Yield 6.6 %
6.6 %
ASTM D638
Flexural Modulus 7.481 GPa
1085 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.694 J/cm
1.30 ft-lb/in
ASTM D256
Gardner Impact 0.904 J

@Temperature 23.0 °C
0.667 ft-lb

@Temperature 73.4 °F
ASTM D5420
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 152 °C
305 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 146 °C
295 °F
ASTM D648