UBE UBEPOL BR153A Oil-Extended BR Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR153A Oil-Extended BR Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 68 | 68 | ASTM D412 |
| Tensile Strength at Break | 18.3 MPa | 2650 psi | ASTM D412 |
| Elongation at Break | 440 % | 440 % | ASTM D412 |
| 100% Modulus | 0.00280 GPa | 0.406 ksi | ASTM D412 |
| 200% Modulus | 0.00730 GPa | 1.06 ksi | ASTM D412 |
| 300% Modulus | 0.0124 GPa | 1.80 ksi | ASTM D412 |
| Rebound | 53 % | 53 % | BS.903,PART22 |
| Tear Strength | 52.0 kN/m | 297 pli | ASTM D624 |
| Abrasion | 98 | 98 | Lombourn Abrasion Index (Iwamoto Seisakusyo, Japan); UBE Method |
| 207 | 207 | Pico Abrasion Index; ASTM D2228 | |
| Compression Set | 13 % | 13 % | Method B, 70°C, 72hrs; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cut Generation De Mattia Flexing Machine | Min 300,000 times | ASTM D430 |
| Cut Growth (2mm-->15mm) De Mattia Flexing Machine | 700 times | ASTM D313 |
| Goodrich Flex, 0.175" Stroke, 55lb, 100°C, P.S. | 6% | ASTM D623 (26°C change in temperature) |
| Wet Skid Resistance on Safety-Walk | 21 | UBE Method (British Portable Skid Resistance Tester) |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 T 30 Polyamide 66, 30% Mineral Filled
- SABIC Innovative Plastics EXTEM XH2315 TPI Resin
- Hong Kun Group 4-tert-Butylphenylboronic Acid Pharmaceutical Intermediate
- Solvay Chemicals Grade A Barium Hydroxide Octahydrate
- SolVin 072GA Polyvinyl Chloride Latex Paste
- Shin-Etsu Silicones KE-3611U Electrically Conductive Silicone Elastomer
- DuPont Teijin Films Melinex® 547 Polyester Film, 400 Gauge
- 3M Scotchcal™ IJ355%-10 Changeable Graphic Film
- ArcelorMittal Save 20-13 Electrical Steel
- 3M Scotch-Weld™ MG100 SF Medical Grade Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved