Tra-Con Tra-Cast 3107 Low Shrinkage Epoxy Casting System

Category Polymer , Adhesive , Thermoset , Epoxy
Manufacturer Tra-Con, Inc.
Trade Name Tra-Cast
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tra-Con Tra-Cast 3107 Low Shrinkage Epoxy Casting System.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRA-CAST 3107 is a versatile epoxy casting system developed for high performance production potting, encapsulating, casting and tooling applications where low shrinkage, easy handling and flowability, and excellent mechanical and electrical properties are required. This formulation has a good pot life and low exotherm properties, and cure at room temperature to a tough, rigid, solid with very low shrinkage characteristics and excellent dimensional stability over a wide temperature range. TRA-CAST 3107 adheres to rigid plastics and laminates, metals, and ceramics, has a low coefficient of thermal expansion, and is readily machined and shaped with ordinary shop tools. The fully cured epoxy system is an excellent electrical insulator which provides good resistance to electrolysis, leakage, and corrosion from water, weather, gases and vapors, and from chemical compounds including mild acids and alkalis, many corrosive salts and salt solutions, petroleum product and lubricants, and other organic and inorganic materials. Information provided by Tra-Con Inc.
Physical Properties Metric English Comments
Specific Gravity 1.59 g/cc
1.59 g/cc
Mixed
Volatile Organic Compounds (VOC) Content 11.62 g/l
11.62 g/l
Water Absorption 0.0010 %
0.0010 %
After 24 hours
Viscosity 22500 cP

@Temperature 25.0 °C
22500 cP

@Temperature 77.0 °F
Mixed (sp #6, 10 rpm)
Mechanical Properties Metric English Comments
Hardness, Shore D 85
85
24 hrs @ 25°C
87
87
4 hrs @ 25°C + 2 hrs @ 65°C
Tensile Strength, Yield 56.5 MPa
8200 psi
Elongation at Yield 2.0 %
2.0 %
Compressive Strength 74.5 MPa
10800 psi
Adhesive Bond Strength 17.9 MPa
2600 psi
Lap shear, alum to alum, 4 hrs @ 25°C + 2 hrs @ 65°C
19.7 MPa
2850 psi
Lap shear, alum to alum, 24 hrs @ 25°C
Thermal Properties Metric English Comments
CTE, linear 66.7 µm/m-°C
37.1 µin/in-°F
Below Tg
183 µm/m-°C
102 µin/in-°F
Above Tg
Maximum Service Temperature, Air 125 °C
257 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Glass Transition Temp, Tg 63.0 °C
145 °F
Ultimate Tg
Electrical Properties Metric English Comments
Volume Resistivity 4.80e+15 ohm-cm
4.80e+15 ohm-cm
Dielectric Constant 4.2

@Frequency 1000 Hz
4.2

@Frequency 1000 Hz
Dielectric Strength 16.1 kV/mm
410 kV/in
Dissipation Factor 0.010

@Frequency 1000 Hz
0.010

@Frequency 1000 Hz
Processing Properties Metric English Comments
Cure Time 360 min
6.00 hour
4 hrs @ 25°C + 2 hrs @ 65°C
1440 min

@Temperature 25.0 °C
24.0 hour

@Temperature 77.0 °F
Pot Life 60 min
60 min
25 grams
90 min
90 min
100 grams
Descriptive Properties Value Comments
Color Black
Mix Ratio, parts by weight 100/50
Resin/Hardener
Thixotropic Index 1.7
10 rpm/100 rpm
Working Life hours 2
100 grams