Toyobo Vylopet® EMC615 PET/PBT Blend
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyethylene Terephthalate (PET) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo Vylopet® EMC615 PET/PBT Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Feature: Flame retardant V-0 UL 94 classApplications: electrical and electronic componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking resistance, chemical & weather resistance, and processability.Information provided by Toyobo Co., Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength, Ultimate | 108 MPa | 15700 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Yield Strength | 147 MPa | 21300 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Yield Strength | 93.0 MPa | 13500 psi | ASTM D695 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Comparative Tracking Index | 220 V | 220 V | IEC test |
Users viewing this material also viewed the following:
- MV Labs PT485 [Pt(NH3)4][PtCl4] Tetramineplatinum(II) tetrachloroplatinate(II)
- Ovation Polymers Nemcon™ H PK DP110/X5 PEEK
- PolyOne Edgetek® ET6620-0020 FRV0 Polyamide 66 (Nylon 66)
- SABIC Innovative Plastics Lexan® HPX8R PC Copolymer (Asia Pacific)
- Kinlead HSS12 Normal Grade Heat Sealable Film (thickness: 20 µm)
- A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer
- A. Schulman PP 3486-01 Polypropylene Homopolymer Polypropylene
- Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, 50% RH
- A. Schulman POLYFLAM™ RPP 1021 General Purpose Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved