Toyobo PELPRENE™ P50DFR Polyester TPE, Flame Resistant
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P50DFR Polyester TPE, Flame Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, Flame ResistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 22 g/10 min @Temperature 230 °C |
22 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 96 | 96 | JIS K6301 |
| Hardness, Shore D | 54 | 54 | ASTM D2240 |
| Tensile Strength at Break | 17.6 MPa | 2550 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| 50% Modulus | 0.0108 GPa | 1.57 ksi | ASTM D638 |
| Flexural Modulus | 0.167 GPa | 24.2 ksi | ASTM D790 |
| Compressive Modulus | 0.00940 GPa | 1.36 ksi | 0.1; ASTM D695 |
| Resilience | 65 | 65 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 108 kN/m | 616 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 17 | 17 | ASTM D1044 |
| Compression Set | 55 % | 55 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 160 µm/m-°C @Temperature 20.0 °C |
88.9 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 215 °C | 419 °F | By DSC |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 170 °C | 338 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.00e+13 ohm-cm | 6.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® ET6620-0020 FRV0 Polyamide 66 (Nylon 66)
- SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific)
- Gouda Vuurvast CURAS 60 S Moldable Refractory Material
- LG Chemical SEETEC T3410 Polypropylene Random Terpolymer
- Saint-Gobain Meldin® 7021 Isostatically Molded Graphite Filled Polyimide
- Styron Magnumâ„¢ 9010 ABS, High Gloss
- SGL Carbon Group SIGRAFIL C® C10 M250 UNS Milled Carbon Fiber, Unsized Carbon Fiber
- Goodfellow Tungsten 75/Rhenium 25 Alloy
- Lubrizol ESTANE® 58562 Ester Based Thermoplastic Polyurethane (European Grade)
- 3M 8420-6 Cold Shrink Connector Insulators
Copyright © lookpolymers.com All Rights Reserved