Total Finathene® LL 6010 FE 18P LLDPE film (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total Finathene® LL 6010 FE 18P LLDPE film (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Linear low density polyethylene made by gas phase process for blown film applications. Advised temperature profile: 190 to 220°C.Information provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	on fluff; ISO 1183
Thickness	25.0 microns	0.984 mil
Melt Flow	1.0 g/10 min @Load 2.16 kg	1.0 g/10 min @Load 4.76 lb	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.0 MPa	1600 psi	ISO 527
Film Tensile Strength at Yield, TD	11.0 MPa	1600 psi	ISO 527
Film Elongation at Break, MD	600 %	600 %	ISO 527
Film Elongation at Break, TD	750 %	750 %	ISO 527
Secant Modulus, MD	0.180 GPa	26.1 ksi	ISO 5527
Secant Modulus, TD	0.200 GPa	29.0 ksi	ISO 5527
Dart Drop Test	170 g	0.375 lb	25µ; ISO 7765-1
Film Tensile Strength at Break, MD	45.0 MPa	6530 psi	ISO 527
Film Tensile Strength at Break, TD	40.0 MPa	5800 psi	ISO 527

Thermal Properties	Metric	English	Comments
Melting Point	124 °C	255 °F	ISO 11357-3

Optical Properties	Metric	English	Comments
Haze	11 %	11 %	25µ; ASTM D 1003

Descriptive Properties	Value	Comments
Food Status	This material conforms to both European and American Food contact regulations.