Total EVA 1010 VN 3 Ethylene Vinyl Acetate Copolymer - Blown Film

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer	Total Atofina
Trade Name	EVA
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total EVA 1010 VN 3 Ethylene Vinyl Acetate Copolymer - Blown Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

EVA 1010 VN 3 is made by a high pressure tubular process. Grade for films with high transparency and high mechanical properties. Contains an antioxidant.Application examples: Stretch film, food packaging.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.929 g/cc	0.929 g/cc	ISO 1183
Vinyl Acetate Content	9.0 %	9.0 %
Thickness	40.0 microns	1.57 mil	for samples tested on this data sheet
	25.0 - 300 microns	0.984 - 11.8 mil	possible range, depending on extrusion conditions
Melt Flow	1.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	7.80 MPa	1130 psi	ISO 527-3
Film Tensile Strength at Yield, TD	6.50 MPa	943 psi	ISO 527-3
Film Elongation at Break, MD	370 %	370 %	ISO 527-3
Film Elongation at Break, TD	600 %	600 %	ISO 527-3
Modulus of Elasticity	0.110 GPa	16.0 ksi	ISO 527-2
Elmendorf Tear Strength, MD	3.30 g/micron	83.8 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	3.70 g/micron	94.0 g/mil	ISO 6383-2
Dart Drop Test	480 g	1.06 lb	ISO 7765-1
Film Tensile Strength at Break, MD	31.0 MPa	4500 psi	ISO 527-3
Film Tensile Strength at Break, TD	28.0 MPa	4060 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	98.0 °C	208 °F	ISO 11357
Vicat Softening Point	82.0 °C	180 °F	ISO 306

Optical Properties	Metric	English	Comments
Haze	3.5 %	3.5 %	ISO 14782

Processing Properties	Metric	English	Comments
Processing Temperature	150 - 180 °C	302 - 356 °F