- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyphthalamide (PPA)
- Polyphthalamide (PPA), Carbon Fiber + PTFE Filled
- Techmer ES Luriblend® PPA GF30 SL2 30% Glass Filled
Techmer ES Luriblend® PPA GF30 SL2 30% Glass Filled
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Carbon Fiber + PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PPA GF30 SL2 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: PTFE + Silicone LubricantFeatures: Lubricated and Good Wear ResistanceInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm @Thickness 3.17 mm |
0.0035 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength | 107 MPa | 15500 psi | ASTM D638 |
| Elongation at Yield | 1.0 % | 1.0 % | ASTM D638 |
| Flexural Yield Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 10.7 GPa | 1550 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm |
1.60 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.2 µm/m-°C | 9.00 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 266 °C | 510 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N 1945 GRN Acrylonitrile-Butadiene Rubber
- Polimeri Europa Europrene® SOL R C2525 Styrene - Butadiene Copolymer
- Nilit Nilamid A3 H G3 ZB 13% Glass Reinforced High Impact PA66
- ExxonMobil ESCOR™ AT 320 Cast Film Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 80-7489 Polyacetal-copolymer, with carbon fiber
- UBE UBEPOL VCR617 Synthetic Rubber (Raw Polymer)
- Plenco 00714 Melamine-Phenolic, Granular, Injection Molded
- Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/48280/1000 Fabric
- Eurostar Staramide BG5H PA6, 25% Glass Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved