Techmer ES HiFill® PP GF50 CC HF BK 50% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 50% Glass Fiber Filler |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PP GF50 CC HF BK 50% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightFeatures: Chemically CoupledAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm @Thickness 3.17 mm |
3.30 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 7.47 J/cm @Thickness 3.17 mm |
14.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.6 µm/m-°C | 12.0 µin/in-°F | ASTM D696 |
| Melting Point | 163 °C | 325 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 310 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.1 kV/mm | 510 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Weartech International WT-4 Cobalt Hardfacing & Wear Resistant Alloy
- Plenco 4568 Phenolic, Granular, Compression Molded
- A. Schulman POLYFORT™ FPP 1477 Mineral Filled, General-Purpose Polypropylene
- Arkema Group Rilsan® MB 3945 Nylon 11, Rotomolding Grade (Conditioned)
- Aaron Industries AAROLENE® ARPE HD 300-2 Black BM High Density Polyethylene, Blow Molding
- Ineos Nova 5460 High Impact Polystyrene (discontinued **)
- Pacific Sintered Materials BT-126 Bronze Powdered Metal
- Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F)
Copyright © lookpolymers.com All Rights Reserved