TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 3.0 PHR Luperco 130XL Peroxide

Category	Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 3.0 PHR Luperco 130XL Peroxide.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and many other high performance polyurethane applications. Millathane 76 can be vulcanized by sulfur or peroxide cured systems.Curing of Millathane®76 can easily be done with many types of peroxides. Millathane76 peroxide vulcanizates have superior compression set, greater heat stability, and are more resistant to reversion than sulfur cures.FormulationLuperco 130XL3.0Millathane 76100.0Stearic Acid0.25Poly AC 617A0.5N-55035.0TP-953.0All information provided by TSE Industries

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	66	66
	70	70	heat aged 70 hours @ 100ºC
Tensile Strength, Yield	24.79 MPa	3596 psi
	25.09 MPa	3639 psi	heat aged 70 hours @ 100ºC
Elongation at Yield	246 %	246 %	heat aged 70 hours @ 100ºC
	300 %	300 %
100% Modulus	0.00451 GPa	0.654 ksi
200% Modulus	0.01531 GPa	2.221 ksi
300% Modulus	0.02468 GPa	3.579 ksi
Tear Strength	50.1 kN/m	286 pli	Die C
Compression Set	25.7 % @Temperature 100 °C, Time 79200 sec	25.7 % @Temperature 212 °F, Time 22.0 hour

Processing Properties	Metric	English	Comments
Cure Time	12.0 min @Temperature 83.3 °C	0.200 hour @Temperature 182 °F