TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.5 PHR Vul-Cup 40KE Peroxide

Category	Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer	TSE Industries, Inc
Trade Name	Millathane®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.5 PHR Vul-Cup 40KE Peroxide.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and many other high performance polyurethane applications. Millathane 76 can be vulcanized by sulfur or peroxide cured systems.Curing of Millathane®76 can easily be done with many types of peroxides. Millathane76 peroxide vulcanizates have superior compression set, greater heat stability, and are more resistant to reversion than sulfur cures.FormulationVul-Cup 40KE2.5Millathane 76100.0Stearic Acid0.25Poly AC 617A0.5N-55035.0TP-953.0All information provided by TSE Industries

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	64	64
	68	68	heat aged 70 hours @ 100ºC
Tensile Strength, Yield	26.21 MPa	3802 psi	heat aged 70 hours @ 100ºC
	26.37 MPa	3825 psi
Elongation at Yield	282.88 %	282.88 %	heat aged 70 hours @ 100ºC
	340 %	340 %
100% Modulus	0.00442 GPa	0.641 ksi
200% Modulus	0.01451 GPa	2.104 ksi
300% Modulus	0.0235 GPa	3.41 ksi
Tear Strength	59.0 kN/m	337 pli	Die C
Compression Set	25.9 % @Temperature 100 °C, Time 79200 sec	25.9 % @Temperature 212 °F, Time 22.0 hour

Processing Properties	Metric	English	Comments
Cure Time	7.00 min @Temperature 83.3 °C	0.117 hour @Temperature 182 °F