- Sumitomo Bakelite North America RX® 3-1-501N-P Mineral Filled Diallyl Phthalate
Sumitomo Bakelite North America RX® 3-1-501N-P Mineral Filled Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Cast, Mineral Filler , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America RX® 3-1-501N-P Mineral Filled Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral filled, flame retardant, diallyl ortho-phthalate molding compound which meets the requirements of ASTM D5948 Type MDG-F.Information provided by Vyncolit, a Sumitomo Bak Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.83 g/cc | 0.0661 lb/in³ | Relative Density; ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | Compression Molding; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.2 MPa | 8010 psi | ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | At Rupture; ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Compressive Strength | 152 MPa | 22000 psi | ASTM D695 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 20.0 °C |
13.9 µin/in-°F @Temperature 68.0 °F |
ASTM E-831 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | As molded; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 30 % | 30 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| 4.3 @Frequency 1000 Hz |
4.3 @Frequency 1000 Hz |
wet; ASTM D150 | |
| Dielectric Strength | 15.8 kV/mm | 401 kV/in | 60Hz, Step-by-Step, wet; ASTM D149 |
| Dissipation Factor | 0.013 @Frequency 1000 Hz |
0.013 @Frequency 1000 Hz |
wet; ASTM D150 |
| 0.016 @Frequency 1e+6 Hz |
0.016 @Frequency 1e+6 Hz |
wet; ASTM D150 | |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black, Blue, Gray, Green | |
| Flammability: Burning, sec | 25 | ASTM D229 |
| Flammability: Ignition, sec | 105 | ASTM D229 |
| Form | Granular | |
| Main Filler | Mineral | |
| Molding Method | Compression, transfer, injection |
Users viewing this material also viewed the following:
- MV Labs PT260 Na2PtBr6 Sodium hexabromoplatinate(IV)
- Pau Tai UNISTAB MS-500 Solid Complex Stabilizer
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 3.0 PHR MBTS
- LyondellBasell Plexar® PX5400 Extrudable Tie-Layer Resin, Anhydride Modified LLDPE
- M. Holland Company CP500 Polypropylene Copolymer
- LATI Larpeek 10 K/40 PEEK, 40% Carbon Fiber Reinforced
- Spartech SP-9030 Economy ABS Sheet
- DuPont Performance Polymers Delrin® SC690 NC010 Acetal (POM) (Unverified Data**)
- Diamond Polymers ABSPC 7801E ABS/PC Extrusion Grade, High Impact, High Heat
Copyright © lookpolymers.com All Rights Reserved