Styron CALIBREâ„¢ 7100-8 Polycarbonate

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	Styron
Trade Name	CALIBRE™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron CALIBREâ„¢ 7100-8 Polycarbonate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CALIBREâ„¢ 7100-8 glass-reinforced resin offers increased modulus and improved heat distortion resistance, with minimal shrinkage. It also offers outstanding UL-94 flammability ratings. CALIBREâ„¢ 7100-8 additive package: No mold release.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/inÂ³	ISO 1183B
Linear Mold Shrinkage, Transverse	0.0020 - 0.0050 cm/cm	0.0020 - 0.0050 in/in	ISO 294-4
Melt Flow	8.0 g/10 min @Load 1.20 kg, Temperature 300 Â°C	8.0 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	58.0 MPa	8410 psi	50 mm/min; ISO 527-2
Tensile Strength, Yield	60.0 MPa	8700 psi	50 mm/min; ISO 527-2
Elongation at Break	6.0 %	6.0 %	50 mm/min; ISO 527-2
Elongation at Yield	4.0 %	4.0 %	50 mm/min; ISO 527-2
Tensile Modulus	3.50 GPa	508 ksi	ISO 527
Izod Impact, Notched	1.10 J/cm	2.06 ft-lb/in	ISO 180/A
Charpy Impact, Notched	1.20 J/cmÂ²	5.71 ft-lb/inÂ²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Vicat Softening Point	150 Â°C	302 Â°F	50Â°C/hr, 50N; ISO 306-B50
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in
	5VA @Thickness 3.00 mm	5VA @Thickness 0.118 in
Ring & Ball Softening Point	>= 125 Â°C	>= 257 Â°F	IEC 60335-1

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	175 V	175 V	IEC 60112