Solvay Specialty Polymers Veradel® 3500 Polyethersulfone (PESU) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Veradel® 3500 Polyethersulfone (PESU) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Veradel polyethersulfone (PESU) is transparent and offers high heat deflection temperatures, excellent toughness and dimensional stability, and resistance to steam, boiling water, and mineral acids. Other desirable properties include thermal stability, creep resistance, and inherent flame resistance. Veradel 3600 is a very high melt flow grade suggested for compounding, especially of glass or carbon fiber reinforced compounds.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Specific Gravity	1.37 g/cc	1.37 g/cc	ASTM D792
Water Absorption	1.9 %	1.9 %	30 days; ASTM D570
	0.50 % @Time 86400 sec	0.50 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0060 cm/cm	0.0060 in/in	ASTM D955
Melt Flow	58 g/10 min @Load 2.16 kg, Temperature 380 °C	58 g/10 min @Load 4.76 lb, Temperature 716 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength	88.9 MPa	12900 psi	ASTM D638
Elongation at Yield	6.5 %	6.5 %	ASTM D638
Tensile Modulus	2.69 GPa	390 ksi	ASTM D638
Flexural Strength	125 MPa	18100 psi	ASTM D790
Flexural Modulus	2.62 GPa	380 ksi	ASTM D790
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	52.0 µm/m-°C	28.9 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	200 °C	392 °F	Unannealed; Injection Molded; ASTM D648
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL 94

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	transparent; thickness not quantified

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.70e+15 ohm-cm	1.70e+15 ohm-cm	ASTM D257
Dielectric Constant	3.5 @Frequency 1000 Hz	3.5 @Frequency 1000 Hz	ASTM D150
	3.51 @Frequency 60.0 Hz	3.51 @Frequency 60.0 Hz	ASTM D150
	3.54 @Frequency 1.00e+6 Hz	3.54 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	15.0 kV/mm	381 kV/in	ASTM D149
Dissipation Factor	0.0017 @Frequency 60.0 Hz	0.0017 @Frequency 60.0 Hz	ASTM D150
	0.0022 @Frequency 1000 Hz	0.0022 @Frequency 1000 Hz	ASTM D150
	0.0056 @Frequency 1.00e+6 Hz	0.0056 @Frequency 1.00e+6 Hz	ASTM D150

Processing Properties	Metric	English
Zone 1	335 - 391 °C	635 - 736 °F
Zone 2	335 - 391 °C	635 - 736 °F
Zone 3	335 - 391 °C	635 - 736 °F
Zone 4	335 - 391 °C	635 - 736 °F
Zone 5	335 - 391 °C	635 - 736 °F
Adapter Temperature	327 - 371 °C	621 - 700 °F
Die Temperature	327 - 371 °C	621 - 700 °F
Melt Temperature	343 - 385 °C	649 - 725 °F
	343 - 391 °C	649 - 736 °F
Mold Temperature	149 - 163 °C	300 - 325 °F
Drying Temperature	177 °C	351 °F
	177 °C	351 °F
Dry Time	2.50 hour	2.50 hour
	2.50 hour	2.50 hour

Descriptive Properties	Value	Comments
Agency Ratings	NSF 61	Tested at 82 °C (180 °F) (Commercial Hot)
Appearance	Transparent - Slight Yellow
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Acid Resistant
	Flame Retardant
	Good Adhesion
	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	Good Thermal Stability
	Good Toughness
	High Flow
	High Heat Resistance
	High Tensile Strength
	Hydrolysis Resistant
	Medium Molecular Weight
	Medium Rigidity
Forms	Pellets
Generic	PESU
Injection Rate	Fast
Processing Method	Compounding
	Injection Molding
RoHS Compliance	RoHS Compliant
Screw Compression Ratio	2.2:1.0
Uses	Compounding