Solvay Specialty Polymers Torlon® 5030 Polyamide-imide (PAI), 30% Glass Fiber

Category Polymer , Thermoplastic , Polyamide-imide (PAI) , Polyamide-Imide, Glass Filled
Manufacturer Solvay Specialty Polymers
Trade Name Torlon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Torlon® 5030 Polyamide-imide (PAI), 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Torlon® 5030 is a 30% glass-fiber reinforced grade of polyamide-imide (PAI) resin. It offers high strength and modulus and exceptional creep resistance. It has thermal expansion characteristics similar to aluminum and therefore excellent dimensional stability.The mechanical properties of Torlon® 5030 resin make it a candidate for metal replacement in high temperature, high stress applications. In addition, it offers outstanding electrical properties, which makes it ideal for high performance parts such as connectors, switches and relays.Features: Flame Retardant; Good Chemical Resistance; Good Compressive Strength; Good Creep Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High Temperature StrengthUses: Aerospace Applications; Aircraft Applications; Automotive Applications; Business Equipment; Connectors; Electrical Housing; Electrical Parts; Electrical/Electronic Applications; Housings; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Oil/Gas Applications; Sealing Devices; Switches; Valves/Valve PartsAdditional Properties: Coefficient of Linear Thermal Expansion - ASTM D696 1.6E-5 cm/cm/°CInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
ASTM D792
Filler Content 30 %
30 %
Glass Fiber
Water Absorption 0.24 %

@Time 86400 sec
0.24 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0025 cm/cm
0.0010 - 0.0025 in/in
Mechanical Properties Metric English Comments
Tensile Strength 221 MPa
32100 psi
ASTM D638
Tensile Stress 205 MPa
29700 psi
ASTM D1708
Tensile Modulus 14.5 GPa
2100 ksi
ASTM D638
Flexural Strength 181 MPa

@Temperature 232 °C
26300 psi

@Temperature 450 °F
ASTM D790
333 MPa

@Temperature 23.0 °C
48300 psi

@Temperature 73.4 °F
ASTM D790
Flexural Modulus 9.86 GPa

@Temperature 232 °C
1430 ksi

@Temperature 450 °F
ASTM D790
11.7 GPa

@Temperature 23.0 °C
1700 ksi

@Temperature 73.4 °F
ASTM D790
Compressive Strength 264 MPa
38300 psi
ASTM D695
Compressive Modulus 7.93 GPa
1150 ksi
ASTM D695
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.30 J/cm
9.93 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 282 °C
540 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+17 ohm-cm
2.00e+17 ohm-cm
ASTM D257
Surface Resistance 1.00e+18 ohm
1.00e+18 ohm
ASTM D257
Dielectric Constant 4.2

@Frequency 1.00e+6 Hz
4.2

@Frequency 1.00e+6 Hz
ASTM D150
4.4

@Frequency 60.0 Hz
4.4

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 33.0 kV/mm
838 kV/in
ASTM D149
Dissipation Factor 0.022

@Frequency 60.0 Hz
0.022

@Frequency 60.0 Hz
ASTM D150
0.050

@Frequency 1.00e+6 Hz
0.050

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 304 °C
579 °F
Nozzle Temperature 371 °C
700 °F
Mold Temperature 199 - 216 °C
390 - 421 °F
Drying Temperature 177 °C

@Time 10800 sec
351 °F

@Time 3.00 hour
Moisture Content <= 0.050 %
<= 0.050 %
Back Pressure 6.89 MPa
999 psi
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Form Pellets
Processing Technique Injection Molding; Machining; Profile Extrusion
RoHS Compliance RoHS Compliant
Screw L/D Ratio 18.0:1.0 to 24.0:1.0