Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Solef® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 6020 PVDF homopolymer has very high viscosity for membranes and lithium batteries. It is available exclusively as powder.Features: Homopolymer; Ultra High ViscosityUses: Batteries; MembranesAdditional Properties: Crystallization Heat - ASTM D3417 47.0 to 52.0 J/g; Heat of Fusion - ASTM D3417 57.0 to 66.0 J/gInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 - 1.80 g/cc | 0.0632 - 0.0650 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.040 % @Time 86400 sec |
<= 0.040 % @Time 24.0 hour |
ISO 62 |
| Melt Flow | <= 2.0 g/10 min @Load 21.6 kg, Temperature 230 °C |
<= 2.0 g/10 min @Load 47.6 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 - 50.0 MPa @Thickness 2.00 mm |
3630 - 7250 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 - 57.0 MPa @Thickness 2.00 mm |
7690 - 8270 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 15 - 50 % | 15 - 50 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 - 10 % | 5.0 - 10 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.60 - 1.70 GPa @Thickness 2.00 mm |
232 - 247 ksi @Thickness 0.0787 in |
1.0 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 171 - 175 °C | 340 - 347 °F | DSC |
| Crystallization Temperature | 133 - 138 °C | 271 - 280 °F | Peak; ASTM D3418 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM E1356 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Form | Powder |
Users viewing this material also viewed the following:
- PolyChem Alloy AquaGard™ 6005M
- LyondellBasell Lupolen® 3226 K LDPE, Film Grade
- MetalTek MTEK M-152 Martensitic Stainless Steel
- Gromax CCP PET 9130-104 30% Glass Filled
- Ferro IP 510 Thick Film Glass
- Teknor Apex Chemlon® 225-15 MG Nylon 6, 25% Mineral Reinforced, 15% Glass Fiber Reinforced
- Ensinger Hydel® PEI-7 Polyetherimide (PEI), Static Dissipative
- ExxonMobil Spartan EP 680
- Cast Nylons Nycast® RX Solid Lubricant Filled Red Cast Nylon 6
- 3M Scotchcal™ ElectroCut™ 7125-20 Graphic Film
Copyright © lookpolymers.com All Rights Reserved