Solvay Specialty Polymers Amodel® HFFR-4133 Polyphthalamide (PPA), 33% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® HFFR-4133 Polyphthalamide (PPA), 33% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® HFFR-4133 is a 33% glass-reinforced, halogen-free, flame retardant polyphthalamide (PPA) resin which offers enhanced processing capabilities for electrical and electronic applications. This resin is rated V-0 by Underwriters Laboratories using the UL94 test and is hot-water moldable. It has high flow and a wide processing window and offers good surface appearance, especially for larger electrical components.Features: Fast Molding Cycle; Flame Retardant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Electrical Properties; Good Stiffness; Halogen Free; High Strength; Hot Water MoldabilityUses: Connectors; Electrical/Electronic ApplicationsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Filler Content 33 %
33 %
Glass Fiber
Water Absorption 0.28 %

@Time 86400 sec
0.28 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0032 cm/cm
0.0032 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Yield 145 - 160 MPa
21000 - 23200 psi
ISO 527-2
Elongation at Break 1.9 - 2.3 %
1.9 - 2.3 %
ISO 527-2
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527-2
Flexural Strength 220 - 230 MPa
31900 - 33400 psi
ISO 178
Flexural Modulus 10.8 GPa
1570 ksi
ISO 178
Izod Impact, Notched (ISO) 7.00 - 8.00 kJ/m²
3.33 - 3.81 ft-lb/in²
Type 1, Notch A; ISO 180
Izod Impact, Unnotched (ISO) 40.0 - 48.0 kJ/m²
19.0 - 22.8 ft-lb/in²
Type 1; ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 12.0 µm/m-°C

@Temperature 100 - 200 °C
6.67 µin/in-°F

@Temperature 212 - 392 °F
2
20.0 µm/m-°C

@Temperature 0.000 - 90.0 °C
11.1 µin/in-°F

@Temperature 32.0 - 194 °F
2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 0.000 - 90.0 °C
44.4 µin/in-°F

@Temperature 32.0 - 194 °F
TMA; ASTM E831
130 µm/m-°C

@Temperature 100 - 200 °C
72.2 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi) 300 °C
572 °F
Unannealed; Flatwise; ISO 75-2/A
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.30e+16 ohm-cm
1.30e+16 ohm-cm
ASTM D257
Dielectric Constant 3.53

@Frequency 1.00e+6 Hz
3.53

@Frequency 1.00e+6 Hz
ASTM D150
3.78

@Frequency 60.0 Hz
3.78

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 26.0 kV/mm

@Thickness 1.60 mm
660 kV/in

@Thickness 0.0630 in
ASTM D149
30.0 kV/mm

@Thickness 0.800 mm
762 kV/in

@Thickness 0.0315 in
ASTM D149
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
ASTM D150
0.012

@Frequency 1.00e+6 Hz
0.012

@Frequency 1.00e+6 Hz
ASTM D150
Comparative Tracking Index >= 600 V
>= 600 V
PLC 0; UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 300 °C
572 °F
Front Barrel Temperature 325 °C
617 °F
Melt Temperature 340 - 350 °C
644 - 662 °F
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Suggested Max
Descriptive Properties Value Comments
Additive Flame Retardant
Availability Asia Pacific
Europe
North America
Color Black; Natural
Form Pellets
Processing Technique Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant