DuPont Performance Polymers Hytrel® RS R4275 BK316 Polyester Elastomer TPC-ET

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel® RS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® RS R4275 BK316 Polyester Elastomer TPC-ET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
55 Shore D Renewably Sourced High Viscosity Polyester Elastomer with Good Heat Ageing Protection Developed for Blow Molding Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.00 g/cc
0.0361 lb/in³
1.17 g/cc
0.0423 lb/in³
ISO 1183
Water Absorption 0.50 %

@Thickness 2.00 mm
 0.50 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
ISO 294-4 2577
Melt Flow 6.0 g/10 min

@Load 10.0 kg,
Temperature 230 °C
 6.0 g/10 min

@Load 22.0 lb,
Temperature 446 °F
 cm³/10min; ISO 1133
6.0 g/10 min

@Load 10.0 kg,
Temperature 230 °C
 6.0 g/10 min

@Load 22.0 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
15s; ISO 868
Tensile Strength at Break 35.0 MPa
5080 psi
ISO 527-1/-2
Tensile Stress 6.40 MPa

@Strain 5.00 %
 928 psi

@Strain 5.00 %
 ISO 527-1/-2
10.0 MPa

@Strain 10.0 %
 1450 psi

@Strain 10.0 %
 ISO 527-1/-2
16.0 MPa

@Strain 50.0 %
 2320 psi

@Strain 50.0 %
 ISO 527-1/-2
21.0 MPa

@Strain 100 %
 3050 psi

@Strain 100 %
 ISO 527-1/-2
2.53 MPa

@Strain 4.51 %,
Temperature 120 °C
 367 psi

@Strain 4.51 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.54 MPa

@Strain 3.88 %,
Temperature 100 °C
 368 psi

@Strain 3.88 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
3.78 MPa

@Strain 5.25 %,
Temperature 90.0 °C
 548 psi

@Strain 5.25 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.80 MPa

@Strain 16.33 %,
Temperature 160 °C
 551 psi

@Strain 16.33 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
4.65 MPa

@Strain 11.14 %,
Temperature 120 °C
 674 psi

@Strain 11.14 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.70 MPa

@Strain 29.42 %,
Temperature 160 °C
 682 psi

@Strain 29.42 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
5.01 MPa

@Strain 9.86 %,
Temperature 100 °C
 727 psi

@Strain 9.86 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.27 MPa

@Strain 42.77 %,
Temperature 160 °C
 764 psi

@Strain 42.77 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
5.76 MPa

@Strain 56.03 %,
Temperature 160 °C
 835 psi

@Strain 56.03 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
5.83 MPa

@Strain 17.76 %,
Temperature 120 °C
 846 psi

@Strain 17.76 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.89 MPa

@Strain 6.53 %,
Temperature 60.0 °C
 854 psi

@Strain 6.53 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
6.21 MPa

@Strain 68.93 %,
Temperature 160 °C
 901 psi

@Strain 68.93 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
6.50 MPa

@Strain 15.83 %,
Temperature 100 °C
 943 psi

@Strain 15.83 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
6.55 MPa

@Strain 24.38 %,
Temperature 120 °C
 950 psi

@Strain 24.38 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.57 MPa

@Strain 12.05 %,
Temperature 90.0 °C
 953 psi

@Strain 12.05 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.80 MPa

@Strain 85.36 %,
Temperature 160 °C
 986 psi

@Strain 85.36 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
7.05 MPa

@Strain 31.0 %,
Temperature 120 °C
 1020 psi

@Strain 31.0 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.33 MPa

@Strain 100.05 %,
Temperature 160 °C
 1060 psi

@Strain 100.05 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
7.44 MPa

@Strain 21.8 %,
Temperature 100 °C
 1080 psi

@Strain 21.8 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.52 MPa

@Strain 6.47 %,
Temperature 40.0 °C
 1090 psi

@Strain 6.47 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
7.54 MPa

@Strain 108.54 %,
Temperature 160 °C
 1090 psi

@Strain 108.54 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
7.55 MPa

@Strain 40.03 %,
Temperature 120 °C
 1100 psi

@Strain 40.03 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.73 MPa

@Strain 116.86 %,
Temperature 160 °C
 1120 psi

@Strain 116.86 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
7.91 MPa

@Strain 48.45 %,
Temperature 120 °C
 1150 psi

@Strain 48.45 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.97 MPa

@Strain 127.94 %,
Temperature 160 °C
 1160 psi

@Strain 127.94 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
8.03 MPa

@Strain 27.18 %,
Temperature 100 °C
 1160 psi

@Strain 27.18 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.09 MPa

@Strain 135.33 %,
Temperature 160 °C
 1170 psi

@Strain 135.33 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
8.19 MPa

@Strain 19.46 %,
Temperature 90.0 °C
 1190 psi

@Strain 19.46 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.21 MPa

@Strain 145.5 %,
Temperature 160 °C
 1190 psi

@Strain 145.5 %,
Temperature 320 °F
 TPE; ISO 11403-1 -2
8.29 MPa

@Strain 57.48 %,
Temperature 120 °C
 1200 psi

@Strain 57.48 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.63 MPa

@Strain 66.51 %,
Temperature 120 °C
 1250 psi

@Strain 66.51 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.64 MPa

@Strain 34.94 %,
Temperature 100 °C
 1250 psi

@Strain 34.94 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.12 MPa

@Strain 42.71 %,
Temperature 100 °C
 1320 psi

@Strain 42.71 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.12 MPa

@Strain 79.75 %,
Temperature 120 °C
 1320 psi

@Strain 79.75 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.13 MPa

@Strain 26.87 %,
Temperature 90.0 °C
 1320 psi

@Strain 26.87 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.41 MPa

@Strain 88.18 %,
Temperature 120 °C
 1360 psi

@Strain 88.18 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.53 MPa

@Strain 50.47 %,
Temperature 100 °C
 1380 psi

@Strain 50.47 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.59 MPa

@Strain 14.98 %,
Temperature 60.0 °C
 1390 psi

@Strain 14.98 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
9.69 MPa

@Strain 33.67 %,
Temperature 90.0 °C
 1410 psi

@Strain 33.67 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.79 MPa

@Strain 99.02 %,
Temperature 120 °C
 1420 psi

@Strain 99.02 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.90 MPa

@Strain 58.24 %,
Temperature 100 °C
 1440 psi

@Strain 58.24 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.3 MPa

@Strain 43.55 %,
Temperature 90.0 °C
 1490 psi

@Strain 43.55 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.31 MPa

@Strain 114.67 %,
Temperature 120 °C
 1495 psi

@Strain 114.67 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
10.44 MPa

@Strain 70.19 %,
Temperature 100 °C
 1514 psi

@Strain 70.19 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.74 MPa

@Strain 77.35 %,
Temperature 100 °C
 1558 psi

@Strain 77.35 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.76 MPa

@Strain 52.81 %,
Temperature 90.0 °C
 1561 psi

@Strain 52.81 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.8 MPa

@Strain 132.12 %,
Temperature 120 °C
 1570 psi

@Strain 132.12 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
10.9 MPa

@Strain 7.67 %,
Temperature 23.0 °C
 1580 psi

@Strain 7.67 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
11.16 MPa

@Strain 87.51 %,
Temperature 100 °C
 1619 psi

@Strain 87.51 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
11.23 MPa

@Strain 62.7 %,
Temperature 90.0 °C
 1629 psi

@Strain 62.7 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
11.46 MPa

@Strain 24.19 %,
Temperature 60.0 °C
 1662 psi

@Strain 24.19 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2