Sichuan Deyang Haton® hGR505 Polyphenylene Sulfide/PA Alloy
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Sulfide (PPS) |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hGR505 Polyphenylene Sulfide/PA Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding, high strengthInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.040 % | 0.040 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0032 cm/cm | 0.0032 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0032 cm/cm | 0.0032 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 110 | 110 | GB/T 3398.2-2008 |
| Tensile Strength | 240 MPa | 34800 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.7 % | 1.7 % | GB/T1040.2-2006 |
| Flexural Strength | 340 MPa | 49300 psi | GB/T 9341-2008 |
| Flexural Modulus | 18.9 GPa | 2740 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 68.0 kJ/m² | 32.4 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.60e+16 ohm-cm | 1.60e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 2.00e+15 ohm | 2.00e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0020 | 0.0020 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- Permabond TA430 Acrylic Adhesive & Initiator
- Westlake Plastics MediPEEK IM Polyetheretherketone for Medical Applications
- Hexcel® HexWeb® CR III 5/32-5052-.0025 Corrosion Resistant Specification Grade Aluminum Honeycomb
- ACC MM850 Low Tear Condensation Cure 2-Part Molding Rubber
- ExxonMobil Oppalyte™ 30 HM-3 OPP Film
- Goodfellow Titanium 78/Aluminum 22 Alloy
- SABIC Innovative Plastics NORYL PX2934 PPE+PS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved